Covestro Makrolon Polycarbonate Resin Transparent PC Raw Material 2800 Pc Plastic Pellet

Physical Properties

Metric

English

Comments

Bulk Density 

0.660 g/cc

0.0238 lb/in³

pellets; ISO 60

Density 

1.20 g/cc

0.0434 lb/in³

ISO 1183-1

Moisture Absorption at Equilibrium 

0.12 %

0.12 %

ISO 62, 50% RH

Water Absorption at Saturation 

0.30 %

0.30 %

ISO 62

Water Vapor Transmission 

15.0 g/m²/day
@Thickness 0.100 mm

0.966 g/100 in²/day
@Thickness 0.00394 in

85% RH, film; ISO 15106-1

Oxygen Transmission 

70.0 cc-mm/m²-24hr-atm
@Thickness 0.0254 mm

178 cc-mil/100 in²-24hr-atm
@Thickness 0.00100 in

2760 cc/m²-24hr-bar; film; b.o. ISO 2556

70.0 cc-mm/m²-24hr-atm
@Thickness 0.100 mm

178 cc-mil/100 in²-24hr-atm
@Thickness 0.00394 in

700 cc/m²-24hr-bar; film; b.o. ISO 2556

Nitrogen Transmission 

13.0 cc-mm/m²-24hr-atm
@Thickness 0.100 mm

33.0 cc-mil/100 in²-24hr-atm
@Thickness 0.00394 in

130 cc/m²-24hr-bar; film; b.o. ISO 2556

13.0 cc-mm/m²-24hr-atm
@Thickness 0.0254 mm

33.0 cc-mil/100 in²-24hr-atm
@Thickness 0.00100 in

510 cc/m²-24hr-bar; film; b.o. ISO 2556

Carbon Dioxide Transmission 

429 cc-mm/m²-24hr-atm
@Thickness 0.0254 mm

1090 cc-mil/100 in²-24hr-atm
@Thickness 0.00100 in

16900 cc/m²-24hr-bar; film; b.o. ISO 2556

430 cc-mm/m²-24hr-atm
@Thickness 0.100 mm

1090 cc-mil/100 in²-24hr-atm
@Thickness 0.00394 in

4300 cc/m²-24hr-bar; film; b.o. ISO 2556

Linear Mold Shrinkage, Flow 

0.0065 cm/cm
@Thickness 2.00 mm

0.0065 in/in
@Thickness 0.0787 in

60x60x2 mm; 500 bar; ISO 294-4

Linear Mold Shrinkage, Transverse 

0.0070 cm/cm
@Thickness 2.00 mm

0.0070 in/in
@Thickness 0.0787 in

60x60x2 mm; 500 bar; ISO 294-4

Melt Flow 

10 g/10 min
@Load 1.20 kg,
Temperature 300 °C

10 g/10 min
@Load 2.65 lb,
Temperature 572 °F

ISO 1133

Mechanical Properties

Metric

English

Comments

Puncture Resistance 

5400 N
@Temperature 23.0 °C

1210 lb (f)
@Temperature 73.4 °F

ISO 6603-2

6300 N
@Temperature -30.0 °C

1420 lb (f)
@Temperature -22.0 °F

ISO 6603-2