Characteristics
- Injection
- Medium impact
- Good flow for process
- High gloss
- High rigidity
Applications
- Tape recorders
- Video cassettes
- Clocks
- Office equipment
- House-ware
Properties | Test | Test Condition | SI unit | |
Unit | s.p. | |||
Rheological Properties | ||||
Specific Gravity Melt Volume Rate
Melt Volume Rate |
ASTM D792 ASTM D1238 ASTM D1238 | 23℃
200℃, 5kg load 220℃, 10kg load |
g/cm3
g/10min g/10min |
1.04
2.1 23.0 |
Mechanical Properties | ||||
Izod Impact Strength Izod Impact Strength Tensile Strength at Yield Tensile Strength at Break Elongation at Break Flexural Yield
Flexural Modulus |
ASTMD256 ASTMD256 ASTMD638 ASTMD638 ASTMD638 ASTMD790
ASTMD790 |
23℃, 1/4” Notched 23℃, 1/8” Notched 23℃, 5 mm/min
23℃, 5 mm/min 23℃, 5 mm/min 23℃, 2.8 mm/min 23℃, 2.8 mm/min |
kg-cm/cm kg-cm/cm kg/cm2 kg/cm2
% kg/cm2 kg/cm2 |
16
16 480 380 20 800 30000 |
Thermal Properties | ||||
Heat Distortion Temperature Vicat Softening Temperature | ASTMD648 ASTMD1525 | unannealing 1.8MPa
50oC/hr , 1 kg load |
℃
℃ |
85
104 |
Physical Properties | ||||
Rockwell Hardness Mold Shrinkage
Moisture Absorption Equilibrium |
ASTMD785 ASTMD955
ASTMD570 |
23℃, R-scale 60×60×2mm SFlow
23°C/50% RH |
R-scale
%
wt % |
119
≦ 0.4 ≦ 0.3 |
Flammability | ||||
UL-94 | 1/16 inch | No E50263 | HB | |
Electrical | ||||
Relative Temperature Index Hot Wire Ignition
High Current Arc Ignition Arc Tracking Rate |
UL-746B UL-746A UL-746A
UL-746A |
0.062 inch above
0.062 inch above 0.062 inch above 0.062 inch above |
℃
Secs Arcs in/min |
60
15 15 0 |
Specification: ABS MOULDING-TAITA-5000S
|