Characteristics
- Injection
- Medium impact
- Good flow for process
- High gloss
- High rigidity
Applications
- 3C exterior parts
- Video cassettes
- Clocks
- Office equipment
- House-ware
Properties | Test | Test Condition | SI unit | |
Unit | s.p. | |||
Rheological Properties | ||||
Specific Gravity
Melt Volume Rate |
ISO 1183
ISO 1133 |
23℃
220℃, 10kg load |
g/cm3
cm3/10min |
1.03
20 |
Mechanical Properties | ||||
Izod Impact Strength | ISO 180/1A | 23℃, Notched | KJ/m2 | 18 |
Charpy impact strength | ISO 179/1A | 23℃, Notched | KJ/m2 | 19 |
Tensile Strength at Yield | ISO 527 | 23℃, 50 mm/min | MPa | 46 |
Tensile Strength at Break | ISO 527 | 23℃, 50 mm/min | MPa | 35 |
Elongation at Break | ISO 527 | 23℃, 50 mm/min | % | 30 |
Flexural Yield | ISO 178 | 23℃, 2.0 mm/min | MPa | 72 |
Flexural Modulus | ISO 178 | 23℃, 2.0 mm/min | GPa | 2.1 |
Thermal Properties | ||||
Heat Distortion Temperature | ISO 75 | unannealing 1.8MPa | ℃ | 84 |
Vicat Softening Temperature | ISO 306 | 50oC/hr , 1 kg load | ℃ | 97 |
Physical Properties | ||||
Rockwell Hardness | ISO 2039-2 | 23℃, R-scale | R-scale | 110 |
Mold Shrinkage | ISO 294-4 | 60×60×2mm SFlow | % | ≦ 0.4 |
Moisture Absorption Equilibrium | ISO 62 | 23°C/50% RH | wt % | ≦ 0.3 |
Flammability | ||||
UL-94 | 1/16 inch | No E50263 | HB | |
Electrical | ||||
Relative Temperature Index | UL-746B | 0.062 inch above | ℃ | 60 |
Hot Wire Ignition | UL-746A | 0.062 inch above | Secs | 17 |
High Current Arc Ignition | UL-746A | 0.062 inch above | Arcs | 200 |
Arc Tracking Rate | UL-746A | 0.062 inch above | in/min | 0 |
Specification: ABS MOULDING-TAITA-5000
|