DESCRIPTION
RB307MO is a random ethylene copolymer with good transparency and contact clarity, very good gloss and surface finish.
This product also features outstanding impact strength.
| Property
Density |
Typical Value
900-910kg/m³ |
Test Method
ISO 1183 |
| Melt Flow Rate (230°C/2.16kg) | 1,5g/10min | ISO 1133 |
| Tensile Modulus (1mm/min) | 900MPa | ISO 527-2 |
| Tensile Strain at Yield (50mm/min) | 13% | ISO 527-2 |
| Tensile Stress at Yield (50mm/min) | 24MPa | ISO 527-2 |
| Flexural Modulus | 900MPa | ISO 178 |
| Flexural Modulus(by 1% secant) | 850MPa | ASTM D790A |
| Tensile Strain at Yield | 13% | ASTM D638 |
| Tensile Stress at Yield | 24MPa | ASTM D638 |
| Charpy Impact Strength, notched (23°C) | 25kJ/m²(PB) | ISO 179/1eA |
| IZOD Impact Strength, notched (23°C) | 300J/m | ASTM D256 |
| Heat Deflection Temperature(0,45MPa)** | 70°C | ISO 75-2 |
| Vicat Softening Temperature(Method A)*** | 120°C | ISO 306 |
| Haze(2mm) | 16% | ASTM D1003 |
| Hardness, Rockwell(R-scale) | 75 | ISO 2039-2 |
Specification: PPR-BOROUGE-RB307MO
|