Characteristics
M312 is a Heterophasic Polypropylene Impact Copolymer (PPiCP), produced by the latest generation Spheripol II Technology. This PPiCP is primarily suitable for Injection Molding process. M312 combines excellent processability with high Flow, low Cycle Time, good Impact – Stiffness balance and good Gloss.
Application
- Automotive Components
- Housewares, Thermowares & Sanitarywares
- Industrial Components
- Luggage
- Paint Pail
- Compounding
| Property | Test Method | Unit | Value |
| Melt Flow Index (2.16 kg & 2300 C) | ASTM D 1238 | g/10 min | 12 |
| Density at 23°C | ASTM D 1505 | g/cm3 | 0.90 |
| Tensile Strength at Yield (50 mm/min) | ASTM D 638
(Type I – with Extensometer) |
MPa | 22 |
| Tensile Elongation at Yield (50 mm/min) | % | 7 | |
| Flexural Modulus | ASTM D 790A | MPa | 1000 |
| Notched Izod Impact Strength (23°C) | ASTM D 256A | J/m | 120 |
| Vicat Softening Point (10N) | ASTM D 1525 | 0C | 145 |
| Heat Deflection Temperature (0.455 MPa) | ASTM D 648 | 0C | 88 |
| Typical Processing Temperature | ||
| Barrel Temperature | 0C | 160 – 250 |
| Mold Temperature | 0C | 30 – 40 |
Specification: PP CP-HALDIA-M312
|