EVA-18% TO 25%-HANWHA-2319
Product Description
HANWHA EVA 2319 is manufactured by Dow tubular high pressure process and designed for variety of foam molding application such as shoes and sandals etc.. EVA 2319 is well known for its excellent processability and high quality assurance.
- Excellent Foam Molding Property
- Very Good Mechanical Properties
- Excellent Loading Property of Various Fillers
- Good Elastic Property of Sponge
| Physical | Nominal Value (English) | Nominal Value (SI) | Test Method | ||
| Density | 0.939 g/cm³ | 0.939 g/cm³ | ASTM D1505 | ||
| Melt Mass-Flow Rate (MFR) (190°C/2.16 | kg) | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 | |
| Vinyl Acetate Content | 19.0 wt% | 19.0 wt% | Internal Method | ||
| Mechanical | Nominal Value (English) | Nominal Value (SI) | Test Method | ||
| Tensile Strength (Break) | 1990 psi | 13.7 MPa | ASTM D638 | ||
| Tensile Elongation (Break) | 800 % | 800 % | ASTM D638 | ||
| Hardness | Nominal Value (English) | Nominal Value (SI) | Test Method | ||
| Durometer Hardness
Shore A |
90 |
90 |
ASTM D2240 | ||
| Shore D | 36 | 36 | |||
| Thermal | Nominal Value (English) | Nominal Value (SI) | Test Method | ||
| Brittleness Temperature | < -105 °F | < -76.0 °C | ASTM D746 | ||
| Vicat Softening Temperature | 138 °F | 59.0 °C | ASTM D1525 | ||
| Melting Temperature | 187 °F | 86.0 °C | ASTM D3417 | ||
| Optical | Nominal Value (English) | Nominal Value (SI) | Test Method | ||
| Gloss (45°) | 82 | 82 | ASTM D2457 | ||
| Additional Information | Nominal Value (English) | Nominal Value (SI) | |||
| Processing Temperature
Kneader |
176 to 212 °F |
80 to 100 °C |
|||
| Roll Mill | 194 °F | 90 °C | |||
Specification: EVA-18% TO 25%-HANWHA-2319
|