Characteristics
M307 is a Heterophasic Polypropylene Impact Copolymer (PPiCP), produced by the latest generation Spheripol II Technology. This PPiCP is primarily suitable for Injection Molding process. M307 combines excellent processability with low Cycle Time
Application
- General Purpose Injection Molding
| Property | Test Method | Unit | Value |
| Melt Flow Index (2.16 kg & 2300 C) | ASTM D 1238 | g/10 min | 7 |
| Density at 23°C | ASTM D 1505 | g/cm3 | 0.90 |
| Tensile Strength at Yield (50 mm/min) | ASTM D 638
(Type I – with Extensometer) |
MPa | 23 |
| Tensile Elongation at Yield (50 mm/min) | % | 6 | |
| Flexural Modulus | ASTM D 790A | MPa | 1000 |
| Notched Izod Impact Strength (23°C) | ASTM D 256A | J/m | 80 |
| Vicat Softening Point (10N) | ASTM D 1525 | 0C | 145 |
| Heat Deflection Temperature (0.455 MPa) | ASTM D 648 | 0C | 88 |
| Typical Processing Temperature | ||
| Barrel Temperature | 0C | 180 – 260 |
| Mold Temperature | 0C | 30 – 40 |
Specification: PP CP-HALDIA-M307
|