General | |||
Availability 1 | • Asia Pacific | ||
Features | • Good Mold Release
• High Flow |
• High Impact Resistance
• High Stiffness |
• Low Odor
• Nucleated |
Uses | • Appliance Components
• Consumer Applications |
• Containers
• Rigid Food Packaging |
• Toys |
Appearance | • Natural Color | ||
Form(s) | • Pellets | ||
Processing Method | • Injection Molding | ||
Revision Date | • 07/01/2010 |
Physical | Typical Value | (English) | Typical Value | (SI) | Test Based On |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 50 | g/10 min | 50 | g/10 min | ASTM D1238 |
Density | 0.900 | g/cm³ | 0.900 | g/cm³ | ExxonMobil Method |
Mechanical | Typical Value | (English) | Typical Value | (SI) | Test Based On |
Tensile Strength at Yield | ASTM D638 | ||||
2.0 in/min (51 mm/min) | 3680 | psi | 25.4 | MPa | |
Tensile Stress at Yield | 3580 | psi | 24.7 | MPa | ISO 527-2/50 |
Elongation at Yield (2.0 in/min (51 mm/min)) | 4.6 | % | 4.6 | % | ASTM D638 |
Tensile Strain at Yield | 3.7 | % | 3.7 | % | ISO 527-2/50 |
Tensile Modulus | 199000 | psi | 1370 | MPa | ISO 527-1/1 |
Flexural Modulus – 1% Secant | |||||
0.051 in/min (1.3 mm/min) | 194000 | psi | 1340 | MPa | ASTM D790A |
0.51 in/min (13 mm/min) | 221000 | psi | 1520 | MPa | ASTM D790B |
Flexural Modulus
(0.079 in/min (2.0 mm/min)) |
184000 | psi | 1270 | MPa | ISO 178 |
Impact | Typical Value | (English) | Typical Value | (SI) | Test Based On |
Notched Izod Impact (73°F (23°C)) | 1.8 | ft·lb/in | 94 | J/m | ASTM D256A |
Notched Izod Impact Strength | ISO 180/1A | ||||
-40°F (-40°C) | 1.9 | ft·lb/in² | 3.9 | kJ/m² | |
0°F (-18°C) | 2.0 | ft·lb/in² | 4.2 | kJ/m² | |
73°F (23°C) | 3.5 | ft·lb/in² | 7.4 | kJ/m² | |
Charpy Notched Impact Strength | ISO 179/1eA | ||||
-22°F (-30°C) | 2.0 | ft·lb/in² | 4.2 | kJ/m² | |
-4°F (-20°C) | 2.2 | ft·lb/in² | 4.6 | kJ/m² | |
32°F (0°C) | 2.6 | ft·lb/in² | 5.4 | kJ/m² | |
73°F (23°C) | 4.0 | ft·lb/in² | 8.5 | kJ/m² | |
Gardner Impact | ASTM D5420 | ||||
-20°F (-29°C), 0.125 in (3.18 mm),
Geometry GC |
147 | in·lb | 16.6 | J | |
Thermal | Typical Value | (English) | Typical Value | (SI) | Test Based On |
Heat Deflection Temperature (1.80 MPa) | 123 | °F | 50.7 | °C | ISO 75-2/A |
Heat Deflection Temperature (0.45 MPa) | 199 | °F | 93.0 | °C | ISO 75-2/Bf |
Deflection Temperature Under Load (DTUL) at 66psi – Unannealed | 221 | °F | 105 | °C | ASTM D648 |
DTUL (66 psi) – Annealed | 246 | °F | 119 | °C | ASTM D648 |
Specification: PP-CP-ExxonMobil-7555KNE2
|