DESCRIPTION
BH975MO is a heterophasic copolymer characterized by optimum combination of very high stiffness, good flow properties and good impact strength.
Articles moulded with this product exhibit good antistatic performance and very good mould release.
Borstar Nucleation Technology (BNT) in combination with excellent stiffness and good flow properties creates a high potential for wall-thickness reduction.
PHYSICAL PROPERTIES
| Property
Density |
Typical Value
900-910kg/m³ |
Test Method
ISO 1183 |
| Melt Flow Rate (230°C/2.16kg) | 38g/10min | ISO 1133 |
| Tensile Modulus (1mm/min) | 1500MPa | ISO 527-2 |
| Tensile Strain at Yield (50mm/min) | 4% | ISO 527-2 |
| Tensile Stress at Yield (50mm/min) | 25MPa | ISO 527-2 |
| Flexural Modulus | 1550MPa | ISO 178 |
| Tensile Strain at Yield | 4% | ASTM D638 |
| Tensile Stress at Yield | 25MPa | ASTM D638 |
| Flexural Modulus(by 1% secant) | 1500MPa | ASTM D790A |
| Charpy Impact Strength, notched (23°C) | 8kJ/m² | ISO 179/1eA |
| Charpy Impact Strength, notched (-20°C) | 4,5kJ/m² | ISO 179/1eA |
| IZOD Impact Strength, notched (23°C) | 80J/m | ASTM D256 |
| IZOD Impact Strength, notched (-20°C) | 55J/m | ASTM D256 |
| Heat Deflection Temperature(0,45MPa)** | 105°C | ISO 75-2 |
| Vicat Softening Temperature(Method A)*** | 150°C | ISO 306 |
| Hardness, Rockwell(R-scale) | 92 | ISO 2039-2 |
Specification: PP-CP-BOROUGE-BH975MO
|