Product Description
Low Viscosity Acetal Homopolymer with Improved Processing
| Physical | Nominal Value Unit | Test Method |
| Density | 1.42 g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 25 g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 21.0 cm³/10min | ISO 1133 |
| Molding Shrinkage
Across Flow |
1.9 % |
ISO 294-4 |
| Flow | 1.9 % | |
| Water Absorption
23°C, 24 hr, 2.00 mm |
1.4 % |
ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.30 % | |
| Mechanical | Nominal Value Unit | Test Method |
| Tensile Modulus | 3300 MPa | ISO 527-2 |
| Tensile Stress (Yield) | 71.0 MPa | ISO 527-2 |
| Tensile Strain (Yield) | 12 % | ISO 527-2 |
| Nominal Tensile Strain at Break | 23 % | ISO 527-2 |
| Tensile Creep Modulus
1 hr |
2800 MPa |
ISO 899-1 |
| 1000 hr | 1500 MPa | |
| Flexural Modulus | 3000 MPa | ISO 178 |
| Impact | Nominal Value Unit | Test Method |
| Charpy Notched Impact Strength
-30°C |
7.0 kJ/m² |
ISO 179/1eA |
| 23°C | 8.0 kJ/m² | |
| Charpy Unnotched Impact Strength
-30°C |
200 kJ/m² |
ISO 179/1eU |
| 23°C | 200 kJ/m² |
Specification: POM-Dupont-Delrin- 900P NC010
|