DESCRIPTION
BD265MO is a very high impact heterophasic copolymer based on proprietary Borstar Nucleation Technology (BNT). This product exhibits excellent impact strength even at low temperatures and good processability and stiffness properties.
Articles produced with this grade exhibit very good demoulding properties and dimensional consistency with respect to different colours.
| Property
Density |
Typical Value
900-910kg/m³ |
ITest Method
SO 1183 |
| Melt Flow Rate (230°C/2.16kg) | 7g/10min | ISO 1133 |
| Tensile Modulus (1mm/min) | 1200MPa | ISO 527-2 |
| Tensile Strain at Yield (50mm/min) | 6% | ISO 527-2 |
| Tensile Stress at Yield (50mm/min) | 22MPa | ISO 527-2 |
| Flexural Modulus | 1250MPa | ISO 178 |
| Charpy Impact Strength, notched (23°C) | No Break | ISO 179/1eA |
| Charpy Impact Strength, notched (-20°C) | 9.0kJ/m² | ISO 179/1eA |
| Charpy Impact Strength, notched (-30°C) | 7.0kJ/m² | ISO 179/1eA |
| IZOD Impact Strength, notched (23°C) | No Break | ASTM D256 |
| IZOD Impact Strength, notched (-20°C) | 110J/m | ASTM D256 |
| Heat Deflection Temperature(0,45MPa)** | 90°C | ISO 75-2 |
| Vicat Softening Temperature(Method A)*** | 142°C | ISO 306 |
| Hardness, Rockwell(R-scale) | 87 | ISO 2039-2 |
Specification: PP-CP-BOROUGE-BD265MO
|