PC MOULDING-LOTTE-LT-1100
| Physical | ||||
| Specific Gravity | ASTM D792 | Natural or
representative color |
– | 1.2 |
| Melt Flow Index | ASTM D1238 | 300℃, 1.2kg | g/10min | 11.5 |
| Mold Shrinkage(MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.5~0.7 |
| Mold Shrinkage(TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.5~0.7 |
| Mechanical | ||||
| Tensile Strength at
Yield |
ASTM D638 | 50mm/min | kgf/㎠ | 640 |
| Tensile Strain at break | ASTM D638 | 50mm/min | % | 110 |
| Tensile Modulus | ASTM D638 | 50mm/min | kgf/㎠ | 23000 |
| Tensile Strength at
break |
ASTM D638 | 50mm/min | kgf/㎠ | 640 |
| Flexural Strength | ASTM D790 | 2.8mm/min | kgf/㎠ | 920 |
| Flexural Modulus | ASTM D790 | 2.8mm/min | kgf/㎠ | 23000 |
| Izod Impact
Strength(notched) |
ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 15 |
| Izod Impact
Strength(notched) |
ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 87 |
| Rockwell Hardness | ASTM D785 | R-Scale | – | 120 |
| Thermal | ||||
| Heat Deflection
Temperature |
ASTM D648 | 18.56kgf/㎠, 6.4mm | °C | 127 |
| Heat Deflection
Temperature |
ASTM D648 | 4.6kgf/㎠, 6.4mm | °C | 137 |
| VICAT Softening
Temperature |
ISO 306 | B/50 | °C | 146 |
| Flammability | ||||
| Flammability | UL94 | V-2 | mm | 0.8, 1.5, 2.0, 2.5, 3.0 |
Specification: PC MOULDING-LOTTE-LT-1100
|