Product Description
20 melt superior processing, fast cycling
Physical | Nominal Value (English) | Nominal Value (SI) | Test Method |
Specific Gravity | 1.20 | 1.20 g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 g/10 min | 20 g/10 min | ASTM D1238 |
Molding Shrinkage – Flow (0.125 in (3.18 mm)) | 5.0E-3 to 7.0E-3 in/in | 0.50 to 0.70 % | ASTM D955 |
Mechanical | Nominal Value (English) | Nominal Value (SI) | Test Method |
Tensile Strength 3 | ASTM D638 | ||
Yield | 9000 psi | 62.1 MPa | |
Break | 9500 psi | 65.5 MPa | |
Tensile Elongation 3 | ASTM D638 | ||
Yield | 6.0 % | 6.0 % | |
Break | 120 % | 120 % | |
Flexural Modulus 3 | 335000 psi | 2310 MPa | ASTM D790 |
Flexural Strength 3 | 13500 psi | 93.1 MPa | ASTM D790 |
Impact | Nominal Value (English) | Nominal Value (SI) | Test Method |
Notched Izod Impact (73°F (23°C)) | 12 ft·lb/in | 640 J/m | ASTM D256 |
Hardness | Nominal Value (English) | Nominal Value (SI) | Test Method |
Rockwell Hardness (M-Scale) | 70 | 70 | ASTM D785 |
Thermal | Nominal Value (English) | Nominal Value (SI) | Test Method |
Deflection Temperature Under Load | ASTM D648 | ||
264 psi (1.8 MPa), Unannealed, 0.250 in (6.35 | |||
mm) | |||
Injection | Nominal Value (English) | Nominal Value (SI) | |
Drying Temperature | 250 °F | 121 °C | |
Drying Time | 3.0 to 4.0 hr | 3.0 to 4.0 hr | |
Drying Time, Maximum | 48 hr | 48 hr | |
Suggested Shot Size | 40 to 60 % | 40 to 60 % | |
Rear Temperature | 480 to 520 °F | 249 to 271 °C | |
Middle Temperature | 500 to 540 °F | 260 to 282 °C | |
Front Temperature | 520 to 560 °F | 271 to 293 °C | |
Nozzle Temperature | 510 to 550 °F | 266 to 288 °C | |
Processing (Melt) Temp | 520 to 560 °F | 271 to 293 °C | |
Mold Temperature | 160 to 200 °F | 71.1 to 93.3 °C | |
Back Pressure | 50.0 to 100 psi | 0.345 to 0.689 MPa | |
Screw Speed | 40 to 70 rpm | 40 to 70 rpm | |
Vent Depth | 1.0E-3 to 3.0E-3 in | 0.025 to 0.076 mm |
Specification: PC-LTL-Colorfast PC200
|