PERMANENCE |
English |
SI Metric |
ASTM TEST |
Primary Additive |
25 % |
25 % |
|
Specific Gravity | 1.32 | 1.32 | D 792 |
Molding Shrinkage
1/8 in (3.2 mm) section |
0.0030 – 0.0050 in/in |
0.30 – 0.50 % |
D 955 |
MECHANICAL
Impact Strength, Izod
notched 1/8 in (3.2 mm) section | 2.5 ft-lbs/in | 133 J/m | D 256 |
unnotched 1/8 in (3.2 mm) section | 15.0 ft-lbs/in | 801 J/m | D 4812 |
Tensile Strength | 15000 psi | 103 MPa | D 638 |
Tensile Elongation | 2.0 – 4.0 % | 2.0 – 4.0 % | D 638 |
Tensile Modulus | 1.10 x 10^6 psi | 7584 MPa | D 638 |
Flexural Strength | 24000 psi | 165 MPa | D 790 |
Flexural Modulus | 0.95 x 10^6 psi | 6550 MPa | D 790 |
ELECTRICAL | |||
Volume Resistivity |
1000 – 9.9E+09 ohm.cm |
1000 – 9.9E+09 ohm.cm |
D 257 |
Surface Resistivity | 1.0E+5 – 9.9E+11 ohm/sq | 1.0E+5 – 9.9E+11 ohm/sq | D 257 |
Surface Resistance | 1.0E+4 – 9.9E+10 ohm | 1.0E+4 – 9.9E+10 ohm | ESD STM11.11 |
Static Decay
MIL-PRF-81705D, 5kV to 50 V, 12% RH |
< 2.00 s |
< 2.00 s |
FTMS101C |
4046.1 | |||
PROPERTY NOTES |
GENERAL PROCESSING FOR INJECTION MOLDING | English | SI Metric | |
Injection Pressure Melt Temperature Mold Temperature Drying
Moisture Content Dew Point |
10000 – 18000 psi
530 – 570 °F 150 – 225 °F 4 hrs @ 175 °F 0.20 % 0 °F |
69 – 124 MPa
277 – 299 °C 66 – 107 °C 4 hrs @ 79 °C 0.20 % -18 °C |
|
PROCESSING NOTES | |||
Desiccant Type Dryer Required. |
Specification: NYLON66-RTP-ESD A 204 H PMS
|