| PHYSICAL PROPERTIES |
STANDARD |
VALUE MEASURE UNITS |
| Density |
ISO 1183 |
1.33 g/cm³ |
| Linear shrinkage at moulding |
|
|
| Longitudinal (0.078in/8,700psi) |
ISO 294-4 |
0.004 ÷ 0.007 in/in |
| Transversal (0.078in/8,700psi) |
ISO 294-4 |
0.004 ÷ 0.007 in/in |
| Dimensional stability |
— |
60 |
| Moisture absorption (in air) |
|
|
| after 24hrs |
ISO 62-4 |
0.27 % |
| MECHANICAL PROPERTIES |
STANDARD |
VALUE MEASURE UNITS |
| CHARPY impact strength |
|
|
| Unnotched, at +73°F |
ISO 179-1eU |
30.37 ft.lb/in² |
| Unnotched, at -4°F |
ISO 179-1eU |
23.36 ft.lb/in² |
| Notched, at +73°F |
ISO 179-1eA |
4.67 ft.lb/in² |
| Notched, at -4°F |
ISO 179-1eA |
3.27 ft.lb/in² |
| Tensile elongation |
|
|
| At yield (0.196 in/min), 73°F |
ISO 527 (1) |
– |
| At yield (0.196 in/min), 140°F |
ISO 527 (1) |
– |
| At yield (0.196 in/min), 195°F |
ISO 527 (1) |
3.7 % |
| At yield (0.196 in/min), 250°F |
ISO 527 (1) |
3.8 % |
| At yield (0.196 in/min), 300°F |
ISO 527 (1) |
4.1 % |
| At break (0.196 in/min), 73°F |
ISO 527 (1) |
2.2 % |
| At break (0.196 in/min), 140°F |
ISO 527 (1) |
3.0 % |
| At break (0.196 in/min), 195°F |
ISO 527 (1) |
4.0 % |
| At break (0.196 in/min), 250°F |
ISO 527 (1) |
5.0 % |
| At break (0.196 in/min), 300°F |
ISO 527 (1) |
5.5 % |
| Tensile strength |
|
|
| At yield (0.196 in/min), 73°F |
ISO 527 (1) |
– |
| At yield (0.196 in/min), 140°F |
ISO 527 (1) |
– |
| At yield (0.196 in/min), 195°F |
ISO 527 (1) |
10200 psi |
| At yield (0.196 in/min), 250°F |
ISO 527 (1) |
7200 psi |
| At yield (0.196 in/min), 300°F |
ISO 527 (1) |
5800 psi |
| At break (0.196 in/min), 73°F |
ISO 527 (1) |
19600 psi |
| At break (0.196 in/min), 140°F |
ISO 527 (1) |
14500 psi |
| At break (0.196 in/min), 195°F |
ISO 527 (1) |
9400 psi |
| At break (0.196 in/min), 250°F |
ISO 527 (1) |
7200 psi |
| At break (0.196 in/min), 300°F |
ISO 527 (1) |
5800 psi |
| Elastic modulus |
|
|
| Tensile (speed 0.04 in/min), at 73°F |
ISO 527 (1) |
1190 kpsi |
| Tensile (speed 0.04 in/min), at 140°F |
ISO 527 (1) |
1000 kpsi |
| Tensile (speed 0.04 in/min), at 195°F |
ISO 527 (1) |
610 kpsi |
| Tensile (speed 0.04 in/min), at 250°F |
ISO 527 (1) |
510 kpsi |
| Tensile (speed 0.04 in/min), at 300°F |
ISO 527 (1) |
390 kpsi |