Polyamide 66 (PA66) based compound.
Heat stabilised. Glass fibres. UL94 V-0 classified, free of halogens-based flame retardants and red phosphorous. Very good mechanical properties. Very good electrical properties.
| PHYSICAL PROPERTIES |
STANDARD |
VALUE MEASURE UNITS |
| Density |
ISO 1183 |
1.40 g/cm³ |
| Linear shrinkage at moulding |
|
|
| Longitudinal (2.0mm/60MPa) |
ISO 294-4 |
0.40 ÷ 0.70 % |
| Transversal (2.0mm/60MPa) |
ISO 294-4 |
0.80 ÷ 1.15 % |
| Dimensional stability |
— |
48 |
| Moisture absorption (in air) |
|
|
| after 24hrs |
ISO 62-4 |
0.27 % |
| MECHANICAL PROPERTIES |
STANDARD |
VALUE MEASURE UNITS |
| CHARPY impact strength |
|
|
| Unnotched, at +23°C |
ISO 179-1eU |
75.0 kJ/m² |
| Notched, at +23°C |
ISO 179-1eA |
8.0 kJ/m² |
| Tensile elongation |
|
|
| At break (5 mm/min), 23°C |
ISO 527 (1) |
3.0 % |
| At break (5 mm/min), 60°C |
ISO 527 (1) |
4.3 % |
| At break (5 mm/min), 90°C |
ISO 527 (1) |
6.2 % |
| At break (5 mm/min), 120°C |
ISO 527 (1) |
7.8 % |
| At break (5 mm/min), 150°C |
ISO 527 (1) |
9.0 % |
| Tensile strength |
|
|
| At break (5 mm/min), 23°C |
ISO 527 (1) |
140 MPa |
| At break (5 mm/min), 60°C |
ISO 527 (1) |
100 MPa |
| At break (5 mm/min), 90°C |
ISO 527 (1) |
80 MPa |
| At break (5 mm/min), 120°C |
ISO 527 (1) |
70 MPa |
| At break (5 mm/min), 150°C |
ISO 527 (1) |
60 MPa |
| Elastic modulus |
|
|
| Tensile (speed 1 mm/min), at 23°C |
ISO 527 (1) |
8500 MPa |
| Tensile (speed 1 mm/min), at 60°C |
ISO 527 (1) |
6000 MPa |
| Tensile (speed 1 mm/min), at 90°C |
ISO 527 (1) |
4000 MPa |
| Tensile (speed 1 mm/min), at 120°C |
ISO 527 (1) |
3500 MPa |
| Tensile (speed 1 mm/min), at 150°C |
ISO 527 (1) |
2700 MPa |