DESCRIPTION
AnteoTM FK1828 is produced using the proprietary Borstar® bimodal terpolymer technology combining outstanding sealing performance with easy processabilty, good optics and superior mechanical properties. Film made with AnteoTM FK1828 exhibits unique combination of low seal initiation (SIT), high hot tack force, excellent puncture and tear properties. AnteoTM FK1828 used in combination with Borstar® PE / BorShape™ PE / LDPE / PP products offers best in class high performance transparent flexible packaging solution with potential for down gauging.
AnteoTM FK1828 contains slip, Antiblock, Antioxidant and Processing Aid (PPA).
PHYSICAL PROPERTIES
| Property |
|
Typical Value* |
Unit |
Test Method |
| Tensile Strength at Break |
MD/TD |
52/50 |
MPa |
ISO 527-3 |
| Elongation at Break |
MD/TD |
650/700 |
% |
ISO 527-3 |
| Tensile Strength at Yield |
TD |
11 |
MPa |
ISO 527-3 |
| Tensile Modulus |
MD/TD |
210/220 |
MPa |
ISO 527-3 |
| Tensile Modulus (1 % Secant) |
MD/TD |
190/200 |
MPa |
ASTM D 882 |
| Elmendorf tear strength |
MD/TD |
550/700 |
g |
ASTM D 1922 |
| Dart Drop |
|
>1000 |
g |
ASTM D 1709/A |
| Coefficient of Friction (Dynamic) |
|
≤0.20 |
|
ASTM D 1894 |
| Haze** |
|
8% |
|
ASTM 1003 |
| Gloss ( 45°)** |
|
60 |
|
ASTM D 2457 |
| Property |
Typical Value* |
Unit |
Test Method |
| Density |
918 |
kg/m³ |
ASTM D 792 |
| Melt Flow Rate MFR (190°C/2.16 kg) |
1.5 |
g/10min |
ASTM D1238 |
| Melting Temperature |
122 |
°C |
ISO 11357/03 |
| Vicat Softening Point |
102 |
°C |
ASTM D 1525 |