| Physical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Density | 0.918 g/cm³ | 0.918 g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Tensile Stress
Yield |
1740 psi |
12.0 MPa |
JIS K6760 |
| Break | 4640 psi | 32.0 MPa | |
| Tensile Strain (Break) | 900 % | 900 % | JIS K6760 |
| Apparent Bending Modulus | 37700 psi | 260 MPa | ASTM D747 |
| Films | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Film Thickness – Tested | 1.2 mil | 30 µm | |
| Tensile Modulus
MD: 1.2 mil (30 µm) |
27600 psi |
190 MPa |
ISO IR 1184 |
| TD: 1.2 mil (30 µm) | 31900 psi | 220 MPa | |
| Tensile Stress
MD: Break, 1.2 mil (30 µm) |
7980 psi |
55.0 MPa |
JIS Z1702 |
| TD: Break, 1.2 mil (30 µm) | 5800 psi | 40.0 MPa | |
| Tensile Elongation
MD: Break, 1.2 mil (30 µm) |
550 % |
550 % |
JIS Z1702 |
| TD: Break, 1.2 mil (30 µm) | 850 % | 850 % | |
| Dart Drop Impact (1.2 mil (30 µm)) | 120 g | 120 g | ASTM D1709 |
| Elmendorf Tear Strength
MD: 1.2 mil (30 µm) |
30 g |
30 g |
ASTM D1922 |
| TD: 1.2 mil (30 µm) | 160 g | 160 g | |
| Hardness | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Durometer Hardness (Shore D) | 55 | 55 | ASTM D2240 |
| Thermal | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Brittleness Temperature | < -94.0 °F | < -70.0 °C | ASTM D746 |
| Vicat Softening Temperature | 216 °F | 102 °C | ASTM D1525 |
| Melting Temperature | 252 °F | 122 °C | DSC |
| Optical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Haze (1.18 mil (30.0 µm)) | 11 % | 11 % | ASTM D1003 |
| Extrusion | Nominal Value (English) | Nominal Value (SI) | |
| Melt Temperature | 374 to 410 °F | 190 to 210 °C | |
| Melt Temperature (Aim) | 392 °F | 200 °C | |
Specification: LL FILM-QAMAR-FC21HN
|