| 71602W is a LLDPE film grade produced by the Spherilene Technology
71602W is without slip additives and antiblock & can be used in General Purpose Packaging Film Application The precise morphological control achieved during polymerization confers good processability & mechanical strengths BIS Designation Code: IS 7328-2B-FBE-BDB |
|||
| Property | Test Method | Unit | Nominal Value |
| Melt Flow Index (2.16 kg, 190°C) | ASTM D1238,
IS 13360 (Part 4/Sec 1) |
g/10 min |
2.5 |
| Melt Flow Index (5 kg, 190°C) | 6.5 | ||
| Melt Flow Index (21.6 kg, 190°C) | ASTM D1238 | g/10 min | 60 |
| Density (23°C) | ASTM D1505,
IS 13360 (Part 3/Sec 11) |
g/cm3 | 0.920 |
| DSC Melting Temperature | ASTM D3418 | °C | 125 |
| Film Property ** | |||
| Tensile Strength at Yield MD |
ASTM D882 (500 mm/min) |
MPa | 12 |
| Tensile Strength at Yield TD | MPa | 11 | |
| Tensile Strength at Break MD | MPa | 23 | |
| Tensile Strength at Break TD | MPa | 19 | |
| Elongation at Break MD | % | 500 | |
| Elongation at Break TD | % | 750 | |
| Elmendorf Tear Strength MD |
ASTM D1922 |
g | 60 |
| Elmendorf Tear Strength TD | g | 280 | |
| Dart Impact Strength, F50 (38 mm Dart, 66 cm Height) | ASTM D1709A | g/µm | 2 |
| Suggested Processing Conditions | |||
| Barrel Temperature | 170 – 200 °C | ||
| Melt Temperature | 190 – 200 °C | ||
| Blow up Ratio | 2.0 – 3.0 °C | ||
| Die Gap | 2.0 – 2.5 °C | ||
* Halene L is the registered trademark of Linear Low Density Polyethylene of Haldia Petrochemicals Limited
Specification: LL FILM-HALDIA-71602W
|