Product Description
LL 1002YB is an LLDPE resin designed for cast films. It offers high gloss and excellent drawdown in both blown and cast film applications. LL1002YB may also be used as a blend partner with LDPE resins to improve film properties and processability
| Resin Properties | Typical Value | (English) | Typical Value | (SI) Test Based On |
| Density | 0.918 | g/cm³ | 0.918 | g/cm³ ExxonMobil Method |
| Melt Index (190°C/2.16 kg) | 2.0 | g/10 min | 2.0 | g/10 min ASTM D1238 |
| Peak Melting Temperature | 248 | °F | 120 | °C ExxonMobil
Method |
| Film Properties | Typical Value | (English) | Typical Value | (SI) Test Based On |
| Tensile Strength at Yield MD | 1100 | psi | 7.4 | MPa ASTM D882 |
| Tensile Strength at Yield TD | 940 | psi | 6.5 | MPa ASTM D882 |
| Tensile Strength at Break MD | 9000 | psi | 60 | MPa ASTM D882 |
| Tensile Strength at Break TD | 3600 | psi | 25 | MPa ASTM D882 |
| Elongation at Break MD | 420 | % | 420 | % ASTM D882 |
| Elongation at Break TD | 830 | % | 830 | % ASTM D882 |
| Secant Modulus MD – 1% Secant | 17000 | psi | 110 | MPa ASTM D882 |
| Secant Modulus TD – 1% Secant | 19000 | psi | 130 | MPa ASTM D882 |
| Dart Drop Impact | < 50 | g | < 50 | g ASTM D1709A |
| Elmendorf Tear Strength MD | 20 | g | 20 | g ASTM D1922 |
| Elmendorf Tear Strength TD | 430 | g | 430 | g ASTM D1922 |
| Puncture Force | 8 | lbf | 36 | N ExxonMobil
Method |
| Puncture Energy | 21 | in·lb | 2.4 | J ExxonMobil
Method |
| Optical Properties | Typical Value | (English) | Typical Value | (SI) Test Based On |
| Gloss (45°) | 98 | 98 | ASTM D2457 | |
| Haze | 1.7 | % | 1.7 | % ASTM D1003 |
Specification: LL FILM-ExxonMobil-1002YB
|