| Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Density | 0.918 | g/cm³ | 0.918 | g/cm³ | ASTM D792 |
| Base Density | 0.918 | g/cm³ | 0.918 | g/cm³ | Dow Method 1 |
| Melt Index (190°C/2.16 kg) | 2.0 | g/10 min | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Film Thickness – Tested | 1.0 | mil | 25 | µm | |
| Film Puncture Force (1.0 mil (25 µm)) | 11.0 | lbf | 48.9 | N | Dow Method |
| Film Puncture Resistance (1.0 mil (25 µm)) | 109 | ft·lb/in³ | 9.02 | J/cm³ | Dow Method |
| Secant Modulus
2% Secant, MD: 1.0 mil (25 µm) |
21600 |
psi |
149 |
MPa |
ASTM D882 |
| 2% Secant, TD: 1.0 mil (25 µm) | 21300 | psi | 147 | MPa | |
| Tensile Strength
MD: Yield, 1.0 mil (25 µm) |
1550 |
psi |
10.7 |
MPa |
ASTM D882 |
| TD: Yield, 1.0 mil (25 µm) | 1300 | psi | 8.94 | MPa | |
| MD: Break, 1.0 mil (25 µm) | 5740 | psi | 39.6 | MPa | |
| TD: Break, 1.0 mil (25 µm) | 2990 | psi | 20.6 | MPa | |
| Tensile Elongation
MD: Break, 1.0 mil (25 µm) |
450 |
% |
450 |
% |
ASTM D882 |
| TD: Break, 1.0 mil (25 µm) | 680 | % | 680 | % | |
| Dart Drop Impact (1.0 mil (25 µm)) | 66 | g | 66 | g | ASTM D1709A |
| Elmendorf Tear Strength
MD: 1.0 mil (25 µm) |
37 |
g |
37 |
g |
ASTM D1922 2 |
| TD: 1.0 mil (25 µm) | 370 | g | 370 | g | |
| Film Stretch Performace – Max Elongation
1.0 mil (25.4 µm) |
230 |
% |
230 |
% |
Dow Method 3 |
| Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Vicat Softening Temperature | 205 | °F | 96.1 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 241 | °F | 116 | °C | Dow Method |
| Optical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Gloss (20°, 1.00 mil (25.4 µm)) | 151 | 151 | ASTM D2457 | ||
| Haze (1.00 mil (25.4 µm)) | 0.56 | % | 0.56 | % | ASTM D1003 |
Specification: LL FILM-DOW-1221P
|