Product Description
ExxonMobil™ LL 1001AV is an ethylene 1-butene linear low density polyethylene resin that offers excellent drawdown and puncture resistance combined with high gloss and clarity. It is frequently used as a blend partner with LDPE resins to improve film properties and processability. TnPP is not intentionally added to LL 1001AV resin.
| Resin Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Density / Specific Gravity |
0.918 |
g/cm³ |
0.918 |
g/cm³ |
ASTM D792 |
| Melt Index (190°C/2.16 kg) |
1.0 |
g/10 min |
1.0 |
g/10 min |
ASTM D1238 |
| Peak Melting Temperature |
248 |
°F |
120 |
°C |
ExxonMobil Method |
| |
|
|
|
|
|
| Thermal |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Vicat Softening Temperature |
207 |
°F |
97.0 |
°C |
ExxonMobil Method |
| |
|
|
|
|
|
| Film Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Tensile Strength at Yield MD |
1400 |
psi |
9.3 |
MPa |
ASTM D882 |
| Tensile Strength at Yield TD |
1500 |
psi |
10 |
MPa |
ASTM D882 |
| Tensile Strength at Break MD |
6500 |
psi |
45 |
MPa |
ASTM D882 |
| Tensile Strength at Break TD |
5200 |
psi |
36 |
MPa |
ASTM D882 |
| Elongation at Break MD |
550 |
% |
550 |
% |
ASTM D882 |
| Elongation at Break TD |
910 |
% |
910 |
% |
ASTM D882 |
| Secant Modulus MD – 1% Secant |
26000 |
psi |
180 |
MPa |
ASTM D882 |
| Secant Modulus TD – 1% Secant |
31000 |
psi |
210 |
MPa |
ASTM D882 |
| Dart Drop Impact |
90 |
g |
90 |
g |
ASTM D1709A |
| Elmendorf Tear Strength MD |
110 |
g |
110 |
g |
ASTM D1922 |
| Elmendorf Tear Strength TD |
450 |
g |
450 |
g |
ASTM D1922 |
| Puncture Force |
9 |
lbf |
40 |
N |
ExxonMobil Method |
| Puncture Energy |
26 |
in·lb |
3.0 |
J |
ExxonMobil Method |
| |
|
|
|
|
|
| Optical Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Gloss (45°) |
51 |
|
51 |
|
ASTM D2457 |
| Haze |
18 |
% |
18 |
% |
ASTM D1003 |