| Physical |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Density |
0.923 |
g/cm³ |
0.923 |
g/cm³ |
ASTM D792 |
| Base Density 1 |
0.923 |
g/cm³ |
0.923 |
g/cm³ |
Dow Method |
| Melt Index (190°C/2.16 kg) |
35 |
g/10 min |
35 |
g/10 min |
ASTM D1238 |
| Environmental Stress-Cracking Resistance (ESCR) |
|
|
|
|
ASTM D1693 |
| 122°F (50°C), 100% Igepal, F50 |
< 1.00 |
hr |
< 1.00 |
hr |
|
| Mechanical |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Tensile Strength |
|
|
|
|
ASTM D638 |
| Yield |
1400 |
psi |
9.65 |
MPa |
|
| Break |
1000 |
psi |
6.89 |
MPa |
|
| Tensile Elongation |
|
|
|
|
ASTM D638 |
| Yield |
4.0 |
% |
4.0 |
% |
|
| Break |
90 |
% |
90 |
% |
|
| Flexural Modulus – 2% Secant |
43000 |
psi |
296 |
MPa |
ASTM D790 |
| Impact |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Tensile Impact Strength 2 |
120 |
ft·lb/in² |
252 |
kJ/m² |
ASTM D1822 |
| Hardness |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Durometer Hardness (Shore D) |
45 |
|
45 |
|
ASTM D2240 |
| Thermal |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Deflection Temperature Under Load |
|
|
|
|
ASTM D648 |
| 66 psi (0.45 MPa), Unannealed |
102 |
°F |
38.9 |
°C |
|
| Brittleness Temperature |
-40.0 |
°F |
-40.0 |
°C |
ASTM D746 |
| Vicat Softening Temperature |
203 |
°F |
95.0 |
°C |
ASTM D1525 |
| Melting Temperature (DSC) |
234 |
°F |
112 |
°C |
Dow Method |
| Peak Crystallization Temperature (DSC) |
205 |
°F |
96.1 |
°C |
Dow Method |