MECHANICAL
| Tensile Strength
Break, Die C, 0.125 in, 20 in/min (3.2mm, 500 mm/min) |
850 psi |
6 MPa |
D 412 |
| Tensile Elongation
Break, Die C, 0.125 in, 20 in/min (3.2mm, 500 mm/min) |
450.0 % |
450.0 % |
D 412 |
| Tensile Stress
Die C 0.125 in, 20 in/min (3.2 mm, 500 mm/min) @ 100 % |
280.0 psi |
1.9 MPa |
D 412 |
| Tear Strength, Die C | 140.0 pli | 24.5 N/mm | D 624 |
| Hardness
Shore A, 10 s delay |
55 |
55 |
D 2240 |
| ELECTRICAL | |||
| Volume Resistivity | < 1E3 ohm.cm | < 1E3 ohm.cm | D 257 |
| Surface Resistivity | < 1E5 ohm/sq | < 1E5 ohm/sq | D 257 |
| Static Decay
MIL-PRF-81705D, 5kV to 50 V, 12% RH |
< 2.00 s |
< 2.00 s |
FTMS101C |
| 4046.1 | |||
| THERMAL | |||
| Ignition Resistance* Flammability** | HB @ 1/16 in | HB @ 1.5 mm | D 635 |
| PROPERTY NOTES |
| GENERAL PROCESSING FOR INJECTION MOLDING |
English |
SI Metric |
|
Injection Pressure |
12000 – 18000 psi |
83 – 124 MPa |
| Melt Temperature | 360 – 410 °F | 182 – 210 °C |
| Mold Temperature | 60 – 150 °F | 16 – 66 °C |
| Drying | 2 hrs @ 175 °F | 2 hrs @ 79 °C |
| Moisture Content | 0.03 % | 0.03 % |
| Dew Point | 0 °F | -18 °C |
| PROCESSING NOTES |
Specification: TEO-RTP-ESD C 2800 B-55A PMS
|
User Reviews
Be the first to review “TEO-RTP-ESD C 2800 B-55A PMS”
Product Enquiry
Related Products
- 1%
TITANIUM DI OXIDE R878 BLUE STAR
Sold by VISHNU INTERNATIONAL
Original price was: ₹240.00.₹238.00Current price is: ₹238.00.
- 4%
ZINC SULPHATE HEPTAHYDRATE 21%
Sold by VISHNU INTERNATIONAL
Original price was: ₹55.00.₹53.00Current price is: ₹53.00.
- 1%
TITANIUM DIOXIDE B101 SILVERSTAR (CHINA)
Sold by VISHNU INTERNATIONAL
Original price was: ₹200.00.₹198.00Current price is: ₹198.00.
There are no reviews yet.