Product Description
LD 100BW is a LDPE containing low antioxidants suitable for the production of LV and MV crosslinked insulation using the 1-step or 2-step silane technology. Through in-house compounding it can also be used in Medium Voltage peroxide cross-linkable insulation. Sufficient antioxidant and Cu-inhibitor should be added to meet specific ageing requirements.
Resin Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
Density |
0.923 |
g/cm³ |
0.923 |
g/cm³ |
ASTM D1505 |
Melt Index (190°C/2.16 kg) |
2.0 |
g/10 min |
2.0 |
g/10 min |
ASTM D1238 |
Peak Melting Temperature |
230 |
°F |
110 |
°C |
ExxonMobil Method |
|
|
|
|
|
|
Molded Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
Tensile Strength at Yield |
1600 |
psi |
11 |
MPa |
ASTM D638 |
Tensile Strength at Break |
1800 |
psi |
13 |
MPa |
ASTM D638 |
Elongation at Yield |
20 |
% |
20 |
% |
ASTM D638 |
Elongation at Break |
490 |
% |
490 |
% |
ASTM D638 |
Flexural Modulus – 1% Secant |
42000 |
psi |
290 |
MPa |
ASTM D790 |
Durometer Hardness (Shore D, 15 sec) |
50 |
|
50 |
|
ASTM D2240 |
|
|
|
|
|
|
Electrical |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
Volume Resistivity |
8.8E+16 |
ohms·cm |
8.8E+16 |
ohms·cm |
ASTM D257 |
Dielectric Constant |
2.2 |
|
2.2 |
|
ASTM D150 |
Dissipation Factor |
4E-4 |
|
4E-4 |
|
ASTM D150 |