| Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Density | 0.925 | g/cm³ | 0.925 | g/cm³ | ASTM D792 |
| Melt Index (190°C/2.16 kg) | 2.0 | g/10 min | 2.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Coefficient of Friction
vs. Itself – Dynamic |
0.15 to 0.20 |
0.15 to 0.20 |
ASTM D1894 | ||
| Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Film Thickness – Tested | 2 | mil | 50 | µm | |
| Secant Modulus
2% Secant, MD : 2.0 mil (50 µm) |
27600 |
psi |
190 |
MPa |
ASTM D882 |
| 2% Secant, TD : 2.0 mil (50 µm) | 30500 | psi | 210 | MPa | |
| Tensile Strength
MD : Yield, 2.0 mil (50 µm) |
1450 |
psi |
10.0 |
MPa |
ASTM D882 |
| TD : Yield, 2.0 mil (50 µm) | 1600 | psi | 11.0 | MPa | |
| MD : Break, 2.0 mil (50 µm) | 3190 | psi | 22.0 | MPa | |
| TD : Break, 2.0 mil (50 µm) | 2900 | psi | 20.0 | MPa | |
| Tensile Elongation
MD : Break, 2.0 mil (50 µm) |
450 |
% |
450 |
% |
ASTM D882 |
| TD : Break, 2.0 mil (50 µm) | 650 | % | 650 | % | |
| Dart Drop Impact (2.0 mil (50 µm)) | 110 | g | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength
MD : 2.0 mil (50 µm) |
450 |
g |
450 |
g |
ASTM D1922 |
| TD : 2.0 mil (50 µm) | 350 | g | 350 | g | |
| Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Vicat Softening Temperature | 205 | °F | 96.0 | °C | ISO 306/A |
Specification: LD FILM-DOW-352E
|