M5002L is a Narrow MWD HDPE produced by Spherilene Technology
M5002L is suited for injection and extrusion-compression molded Caps & Closures
The precise control of morphology & MWD during polymerization confers superior processability, excellent organoleptics & improved performance properties compared to conventional HDPE grades
| Property | Test Method | Unit | Value |
| Melt Flow Index (2.16 kg, 190°C) | ASTM D1238 | g/10 min | 2.5 |
| Density (23°C) | ASTM D1505 | g/cm3 | 0.95 |
| Physical Property | |||
| Tensile Strength at Yield | ASTM D638 | MPa | 25 |
| Tensile Strength at Break | (50 mm/min) | MPa | 30 |
| Elongation at Break | % | >700 | |
| Notched Izod Impact Strength (23°C) | ASTM D256A | J/m | 180 |
| Flexural Modulus | ASTM D790A | MPa | 950 |
| Hardness | ASTM D2240 | Shore D | 61 |
| Vicat Softening Point (10 N) | ASTM D1525 | °C | 125 |
| Heat Deflection Temperature (0.455 MPa) | ASTM D648 | °C | 78 |
| DSC Melting Temperature | ASTM D3418 | °C | 131 |
| Suggested Processing Conditions | |||
| Barrel Temperature | °C | 160 – 190 |
Specification: HD-HALDIA-M5002L
|