| Physical |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Density |
0.955 |
g/cm³ |
0.955 |
g/cm³ |
ASTM D792 |
| Base Density 1 |
0.955 |
g/cm³ |
0.955 |
g/cm³ |
Dow Method |
| Melt Index (190°C/2.16 kg) |
25 |
g/10 min |
25 |
g/10 min |
ASTM D1238 |
| Environmental Stress-Cracking Resistance (ESCR) |
|
|
|
|
ASTM D1693 |
| 122°F (50°C), 100% Igepal, F50 |
1.00 |
hr |
1.00 |
hr |
|
| Mechanical |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Tensile Strength |
|
|
|
|
ASTM D638 |
| Yield |
3700 |
psi |
25.5 |
MPa |
|
| Break |
2000 |
psi |
13.8 |
MPa |
|
| Tensile Elongation |
|
|
|
|
ASTM D638 |
| Yield |
6.0 |
% |
6.0 |
% |
|
| Break |
200 |
% |
200 |
% |
|
| Flexural Modulus – 2% Secant |
136000 |
psi |
938 |
MPa |
ASTM D790B |
| Impact |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Tensile Impact Strength 2 |
60.0 |
ft·lb/in² |
126 |
kJ/m² |
ASTM D1822 |
| Hardness |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Durometer Hardness (Shore D) |
59 |
|
59 |
|
ASTM D2240 |
| Thermal |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Deflection Temperature Under Load |
|
|
|
|
ASTM D648 |
| 66 psi (0.45 MPa), Unannealed |
153 |
°F |
67.2 |
°C |
|
| Brittleness Temperature |
< -105 |
°F |
< -76.1 |
°C |
ASTM D746 |
| Vicat Softening Temperature |
262 |
°F |
128 |
°C |
ASTM D1525 |
| Melting Temperature (DSC) |
264 |
°F |
129 |
°C |
Dow Method |
| Peak Crystallization Temperature (DSC) |
241 |
°F |
116 |
°C |
Dow Method |
There are no reviews yet.