DESCRIPTION
BorPure™MB6562 is a multimodal, high-density polyethylene intended for both injection and compression moulding. This grade combines good organoleptic properties and very good flow properties with a controlled torque level due to the incorporation of slip agent.
The broad molecular weight distribution guarantees superior environmental stress crack resistance.
PHYSICAL PROPERTIES
| Property
Density |
Typical Value*
955 kg/m³ |
Test Method
ISO 1183 |
| Melt Flow Rate (190°C/2.16kg) | 1.5 g/10min | ISO 1133 |
| Tensile Modulus (1mm/min) | 920 MPa | ISO 527-2 |
| Tensile Stress at Yield (50mm/min) | 24.0 MPa | ISO 527-2 |
| Tensile Strain at Yield (50mm/min) | 9.5 % | ISO 527-2 |
| Tensile Stress at Break (50mm/min) | 14.0 MPa | ISO 527-2 |
| Tensile Strain at Break (50mm/min) | 400 % | ISO 527-2 |
| Flexural modulus (2mm/min) | 980 MPa | ISO 178 |
| Charpy Notched Strength (23°C, 1eA, Edgewise) | 14.0 kJ/m² | ISO 179-1 |
| Shore Hardness (Shore D, 15 sec.) | 60.0 | ISO 868 |
| Shore Hardness (Shore D, 1 sec.) | 63.5 | ASTM D2240 |
| VICAT Softening Temperature (A50) | 125°C | ISO306 |
| VICAT Softening Temperature (B50) | 70°C | ISO306 |
| Temperature of deflection under load (DTUL) | 64°C | ISO 75-2 |
| ESCR (10% Igepal – F50) | 400 Hours | ASTM D1693-B |
| FNCT (2% Arkopal, 6.0Mpa, 50°C) | 40 Hours | ISO 16770 |
Specification: HD-BOROUGE-MB6562
|