ASA+PC-Bayblend-ABS T85 XF
@ Plastic Dealer Ask owner
Product Description
(PC+ABS) blend; unreinforced; injection molding grade; Vicat/B 120 temperature = 130 °C; better flow than T85.
| Physical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Density (73°F (23°C)) | 1.14 g/cm³ | 1.14 g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 1.16 in³/10min | 19.0 cm³/10min | ISO 1133 |
| Molding Shrinkage 4 | ISO 2577 | ||
| Across Flow : 500°F (260°C), 0.118 in (3.00
mm) |
0.50 to 0.70 % | 0.50 to 0.70 % | |
| Flow : 500°F (260°C), 0.118 in (3.00 mm) | 0.50 to 0.70 % | 0.50 to 0.70 % | |
| Water Absorption | ISO 62 | ||
| Saturation, 73°F (23°C) | 0.70 % | 0.70 % | |
| Equilibrium, 73°F (23°C), 50% RH | 0.20 % | 0.20 % | |
| Mechanical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Tensile Modulus (73°F (23°C)) | 334000 psi | 2300 MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 73°F (23°C) | 7830 psi | 54.0 MPa | |
| Break, 73°F (23°C) | 7250 psi | 50.0 MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 73°F (23°C) | 4.7 % | 4.7 % | |
| Break, 73°F (23°C) | > 50 % | > 50 % | |
| Impact | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Notched Izod Impact Strength | ISO 180/A | ||
| -22°F (-30°C) | 17 ft·lb/in² | 35 kJ/m² | |
| 73°F (23°C) | 23 ft·lb/in² | 48 kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| -22°F (-30°C) | No Break | No Break | |
| 73°F (23°C) | No Break | No Break | |
| Thermal | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Heat Deflection Temperature | |||
| 66 psi (0.45 MPa), Unannealed | 261 °F | 127 °C | ISO 75-2/B |
| 264 psi (1.8 MPa), Unannealed | 228 °F | 109 °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| — | 262 °F | 128 °C | ISO 306/B50 |
| — | 266 °F | 130 °C | ISO 306/B120 |
Specification: ASA+PC-Bayblend-ABS T85 XF
|