ABS MOULDING 5000W TAITA granuals Delhi plastic Dealer Importer

ABS MOULDING-TAITA-5000W

Add to compare

Characteristics

Applications

Properties	Test	Test Condition	SI unit
Properties	Test	Test Condition	Unit	s.p.
Rheological Properties
Specific Gravity Melt Volume Rate	ISO 1183 ISO 1133	23℃ 220℃, 10kg load	g/cm3 cm3/10min	1.03 19
Mechanical Properties
Izod Impact Strength	ISO 180/1A	23℃, Notched	KJ/m2	19
Charpy impact strength	ISO 179/1A	23℃, Notched	KJ/m2	20
Tensile Strength at Yield	ISO 527	23℃, 50 mm/min	MPa	48
Tensile Strength at Break	ISO 527	23℃, 50 mm/min	MPa	37
Elongation at Break	ISO 527	23℃, 50 mm/min	%	30
Flexural Yield	ISO 178	23℃, 2.0 mm/min	MPa	76
Flexural Modulus	ISO 178	23℃, 2.0 mm/min	GPa	2.2
Thermal Properties
Heat Distortion Temperature	ISO 75	unannealing 1.8MPa	℃	85
Vicat Softening Temperature	ISO 306	50oC/hr , 1 kg load	℃	102
Physical Properties
Rockwell Hardness	ISO 2039-2	23℃, R-scale	R-scale	110
Mold Shrinkage	ISO 294-4	60×60×2mm SFlow	%	≦ 0.4
Moisture Absorption Equilibrium	ISO 62	23°C/50% RH	wt %	≦ 0.3
Flammability
	UL-94	1/16 inch	No E50263	HB
Electrical
Relative Temperature Index	UL-746B	0.062 inch above	℃	85
Hot Wire Ignition	UL-746A	0.062 inch above	Secs	17
High Current Arc Ignition	UL-746A	0.062 inch above	Arcs	200
Arc Tracking Rate	UL-746A	0.062 inch above	in/min	0

Specification: ABS MOULDING-TAITA-5000W

ALPHA	T
Group	ABS
Class	ABS MOULDING
GRADE	5000W
MFI	19
PROCESS	MOULDING
Country	China- TAIWAN
Tds-Name	ABS_5000W_ISO_en.pdf
Tds-Url	https://sourcechatapp-media.s3.ap-south-1.amazonaws.com/60ab3f9a1861530748d090c7/ABS_5000W_ISO_en.pdf
D-Type	S
Brand	T>TAITA