Description
SAHARA C 160HM is a nucleated heterophasic copolymer, suitable for injection molding applications, and contains an anti- static agent. It exhibits a high stiffness combined with a medium fluidity. Sahara C 160HM is extensively used in housewares, furniture, cylindrical containers and crate. This grade is not intended for medical and pharmaceutical applications.
Product Characteristics
Commercial: Active.
Processing Method: Injection Molding.
Typical applications: Crates, Housewares, Opaque containers and Pails.
| Typical Properties | Test Method | Nominal Value | Unit |
| Physical | |||
| Density | ISO1183-1 | 0.90 | g/cm³ |
| Melt Flow Rate 230 °C/2.16 kg. | ISO1133 | 16 | g/10 min |
| Mechanical | |||
| Flexural Modulus | ISO 178 | 1577 | MPa |
| Tensile Modulus | ISO 527-1, -2 | 1520 | MPa |
| Tensile Stress at Yield | ISO 527-1, -2 | 25 | MPa |
| Tensile Strain at Yield | ISO 527-1, -2 | 4 | % |
| Tensile Strain at Break | ISO 527-1, -2 | 36 | % |
| Charpy Impact Notched, Type 1, Edgewise, Notch A, 23 °C | ISO 179 | 9.50 | kJ/m² |
| Charpy Impact Notched, Type 1, Edgewise, Notch A, 0 °C | ISO 179 | 6.50 | kJ/m² |
| Charpy Impact Notched, Type 1, Edgewise, Notch A, -20 °C | ISO 179 | 4.80 | kJ/m² |
| Notched Izod Impact Strength, 23 °C | ISO 180 | 7.80 | J/m |
| Thermal | |||
| Heat Deflection Temperature-A, 1.8 MPa, unannealed | ISO 75B-1, -2 | 56 | °C |
| Heat Deflection Temperature -B, 0.45 MPa, unannealed | ISO 75B-1, -2 | 101 | °C |
| Vicat Softening Temperature, A50 | ISO 306 | 146 | °C |
| Vicat Softening Temperature, B50 | ISO 306 | 67 | °C |
| Processing Condition | |||
| Barrel temperature range: 210 -250 °C
Mold temperature: 15 -40 °C Melt temperature: 240 -260 °C Mold Shrinkage: 1 – 2.5 % |
|||
Specification: PP-CP-SAHARA-C160HM
|
There are no reviews yet.