DESCRIPTION
RE420MO is a versatile designed transparent polypropylene random ethylene copolymer with medium melt flow rate intended for injection moulding and injection stretch blow moulding.
RE420MO is suitable for high speed injection moulding due to clarification and excellent demoulding properties. Articles originating from this product have excellent transparency, good organoleptic properties, good balance of stiffness and impact strength at ambient and refrigerator temperatures, low blooming, good denesting performance and excellent hinge properties.
| Density |
900-910 kg/m³ |
ISO 1183 |
| Melt Flow Rate (230 °C/2,16 kg) |
13 g/10min |
ISO 1133 |
| Tensile Modulus (1 mm/min) |
1100 MPa |
ISO 527-2 |
| Tensile Strain at Yield (50 mm/min) |
12 % |
ISO 527-2 |
| Tensile Stress at Yield (50 mm/min) |
28 MPa |
ISO 527-2 |
| Flexural modulus (5 mm/min) |
1150 MPa |
ISO 178 |
| Flexural modulus (by 1% secant) |
1100 MPa |
ASTM D790A |
| Tensile Strain at Yield |
12 % |
ASTM D738 |
| Tensile Stress at Yield |
28 MPa |
ASTM D738 |
| Charpy Impact Strength, notched (23 °C) |
6 kJ/m² |
ISO 179/1eA |
| IZOD Impact Strength, notched (23 °C) |
65 J/m |
ASTM D256 |
| Heat Deflection Temperature (0,45 N/mm²)* |
75 °C |
ISO 75-2 |
| Vicat Softening Temperature (Method A) ** |
124.5 °C |
ISO 306 |
| Haze ( 2mm ) |
20 % |
ASTM D1003 |
| Hardness, Rockwell (R-scale) |
91 |
ISO 2039-2 |
There are no reviews yet.