PP+MF-LG-LUPOL GP3200
Material Notes:
Description: Injection Molding, PP+MF10%, General PurposeApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0 and 14807-96-6Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0090 – 0.014 cm/cm
@Thickness 3.20 mm |
0.0090 – 0.014 in/in
@Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min
@Load 2.16 kg, Temperature 230 °C |
10 g/10 min
@Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 36.3 MPa
@Thickness 3.20 mm |
5260 psi
@Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 25 %
@Thickness 3.20 mm |
25 %
@Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 48.1 MPa
@Thickness 6.40 mm |
6970 psi
@Thickness 0.252 in |
30mm/min; ASTM D790 |
| Flexural Modulus | 2.75 GPa
@Thickness 6.40 mm |
398 ksi
@Thickness 0.252 in |
30mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.294 J/cm
@Thickness 6.40 mm, Temperature -10.0 °C |
>= 0.551 ft-lb/in
@Thickness 0.252 in, Temperature 14.0 °F |
ASTM D256 |
| >= 0.392 J/cm
@Thickness 6.40 mm, Temperature 23.0 °C |
>= 0.735 ft-lb/in
@Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa | 140 °C | 284 °F | |
Specification: PP+MF-LG-LUPOL GP3200
|