PP THERMOFORMING-BOROUGE-HC205TF
@ Plastic Dealer Ask owner
DESCRIPTION
HC205TF is a polypropylene Homopolymer produced by the proprietary Borstar® process, intended for sheet and thermoformed packaging applications.
This product is produced using the Borstar Nucleation Technology (BNT). Its increased crystallization temperature allows reduced cycle time and increased output. Articles originating from this product have excellent transparency, good organoleptic properties, good balance of stiffness and impact strength at ambient temperatures.\
PHYSICAL PROPERTIES
| Property
Density |
Typical Value
900-910kg/m³ |
Test Method
ISO 1183 |
| Melt Flow Rate (230°C/2.16kg) | 4g/10min | ISO 1133 |
| Tensile Modulus (1mm/min) | 1750MPa | ISO 527-2 |
| Tensile Strain at Yield (50mm/min) | 8% | ISO 527-2 |
| Tensile Stress at Yield (50mm/min) | 35,5MPa | ISO 527-2 |
| Flexural Modulus | 1750MPa | ISO 178 |
| Tensile Strain at Yield | 8% | ASTM D638 |
| Tensile Stress at Yield | 35,5MPa | ASTM D638 |
| Flexural Modulus(by 1% secant) | 1700MPa | ASTM D790A |
| Charpy Impact Strength, notched (23°C) | 5kJ/m² | ISO 179/1eA |
| IZOD Impact Strength, notched (23°C) | 40J/m | ASTM D256 |
| Heat Deflection Temperature(0,45MPa)** | 107°C | ISO 75-2 |
| Vicat Softening Temperature(Method A)*** | 145°C | ISO 306 |
| Hardness, Rockwell(R-scale) | 106 | ISO 2039-2 |
Specification: PP THERMOFORMING-BOROUGE-HC205TF
|