Description
Luban polypropylene is manufactured using Novolen vertical stirred Gas-phase polymerization process. Luban HP2100S is a Homopolymer polypropylene with good flowability and stiffness for general applications.
Application
Thin walled packaging, household articles & general purpose injection molding
Properties (Typical Values)
| Property | Units | Test method | Value |
| Melt flow rate (230°C/2.16 kg) | g/10 min | ISO 1133 | 33 |
| Density | g /cm³ | ISO 1183 | 0.91 |
| Tensile modulus (1 mm/min) | MPa | ISO 527-2 | 1600 |
| Tensile stress at yield (50 mm/min) | MPa | ISO 527-2 | 35 |
| Tensile strain at yield (50 mm/min) | % | ISO 527-2 | 7.5 |
| Tensile strain at break (50 mm/min) | % | ISO 527-2 | 25 |
| Charpy notched impact strength (+23°C) | kJ/m² | ISO 179/1eA | 2 |
| Izod notched impact strength (+23°C) | J/m | ASTM D256 | 20 |
| Heat Deflection Temperature (0.45 MPa) | °C | ISO 75-2 | 85 |
Specification: PP LAMINATION-LUBAN-HP2100S
|