DESCRIPTION
BF970MO is a heterophasic copolymer characterized by an optimum combination of very high stiffness and high impact strength.
This product uses Borstar Nucleation Technology (BNT) to increase productivity by cycle time reduction. BNT, in combination with excellent stiffness and good flow properties, creates a high potential for wall-thickness reduction. Articles moulded with this product exhibit good antistatic performance and very good mould release. They have well-balanced mechanical properties and excellent dimension consistency with respect to different colors
PHYSICAL PROPERTIES
| Property ‘
Density |
Typical Value
900-910kg/m³ |
Test Method
ISO 1183 |
| Melt Flow Rate (230°C/2.16kg) | 20g/10min | ISO 1133 |
| Tensile Modulus (1mm/min) | 1500MPa | ISO 527-2 |
| Tensile Strain at Yield (50mm/min) | 5% | ISO 527-2 |
| Tensile Stress at Yield (50mm/min) | 27MPa | ISO 527-2 |
| Flexural Modulus | 1450MPa | ISO 178 |
| Tensile Strain at Yield | 5% | ASTM D638 |
| Tensile Stress at Yield | 27MPa | ASTM D638 |
| Flexural Modulus(by 1% secant) | 1400MPa | ASTM D790A |
| Charpy Impact Strength, notched (23°C) | 9kJ/m² | ISO 179/1eA |
| Charpy Impact Strength, notched (-20°C) | 4,5kJ/m² | ISO 179/1eA |
| IZOD Impact Strength, notched (23°C) | 95J/m | ASTM D256 |
| IZOD Impact Strength, notched (-20°C) | 55J/m | ASTM D256 |
| Heat Deflection Temperature(0,45MPa)** | 102°C | ISO 75-2 |
| Vicat Softening Temperature(Method A)*** | 149°C | ISO 306 |
| Hardness, Rockwell(R-scale) | 92 | ISO 2039-2 |
Specification: PP-CP-BOROUGE-BF970MO
|
There are no reviews yet.