DESCRIPTION
BD950MO is a heterophasic copolymer intended for compression and injection moulding. The main features of this product are good stiffness, creep and impact resistance, very good processability, high melt strength and extremely low tendency to stress whitening.This product uses Borstar Nucleation Technology (BNT) to increase productivity by cycle time reduction. As with all BNT products, BD950MO exhibits excellent dimensional consistency with different colour additives. This polymer contains slip and antistatic additives to ensure good demoulding properties, low dust attraction and low friction coefficient, meeting the industry standards for closure opening torques.
| Property
Density |
Typical Value
900-910kg/m³ |
Test Method
ISO 1183 |
| Melt Flow Rate (230°C/2.16kg) | 7g/10min | ISO 1133 |
| Tensile Modulus (1mm/min) | 1500MPa | ISO 527-2 |
| Tensile Strain at Yield (50mm/min) | 6% | ISO 527-2 |
| Tensile Stress at Yield (50mm/min) | 30MPa | ISO 527-2 |
| Flexural Modulus | 1450MPa | ISO 178 |
| Tensile Strain at Yield | 7% | ASTM D638 |
| Tensile Stress at Yield | 30MPa | ASTM D638 |
| Flexural Modulus(by 1% secant) | 1450MPa | ASTM D790A |
| Charpy Impact Strength, notched (23°C) | 8kJ/m² | ISO 179/1eA |
| Charpy Impact Strength, notched (-20°C) | 4kJ/m² | ISO 179/1eA |
| IZOD Impact Strength, notched (23°C) | 85J/m | ASTM D256 |
| IZOD Impact Strength, notched (-20°C) | 50J/m | ASTM D256 |
| Heat Deflection Temperature(0,45MPa)** | 100°C | ISO 75-2 |
| Vicat Softening Temperature(Method A)*** | 149°C | ISO 306 |
| Hardness, Rockwell(R-scale) | 92 | ISO 2039-2 |
Specification: PP-CP-BOROUGE-BD950MO
|