| Property |
Test Condition |
Unit |
Standard |
guide value 1 |
|
| |
|
|
|
d.a.m. cond. |
| Rheological properties |
|
|
|
|
| C Molding shrinkage, parallel |
60x60x2; 280 °C / MT 80
°C; 600 bar |
% |
ISO 294-4 |
0.3 |
|
| C Molding shrinkage, transverse |
60x60x2; 280 °C / MT 80
°C; 600 bar |
% |
ISO 294-4 |
0.69 |
|
| Post- shrinkage, parallel |
60x60x2; 120 °C; 4 h |
% |
ISO 294-4 |
0.06 |
|
| Post- shrinkage, transverse |
60x60x2; 120 °C; 4 h |
% |
ISO 294-4 |
0.13 |
|
| Mechanical properties (23 °C/50 % r. h.) |
|
|
|
|
|
| C Tensile modulus |
1 mm/min |
MPa |
ISO 527-1,-2 |
9500 |
5800 |
| C Tensile Stress at break |
5 mm/min |
MPa |
ISO 527-1,-2 |
170 |
100 |
| C Tensile Strain at break |
5 mm/min |
% |
ISO 527-1,-2 |
3.5 |
6.0 |
| C Tensile creep modulus |
1 h |
MPa |
ISO 899-1 |
|
5100 |
| C Tensile creep modulus |
1000 h |
MPa |
ISO 899-1 |
|
4100 |
| C Charpy impact strength |
23 °C |
kJ/m² |
ISO 179-1eU |
75 |
90 |
| C Charpy impact strength |
-30 °C |
kJ/m² |
ISO 179-1eU |
65 |
60 |
| C Charpy notched impact strength |
23 °C |
kJ/m² |
ISO 179-1eA |
10 |
20 |
| C Charpy notched impact strength |
-30 °C |
kJ/m² |
ISO 179-1eA |
< 10 |
10 |
| Izod impact strength |
23 °C |
kJ/m² |
ISO 180-1U |
65 |
80 |
| Izod impact strength |
-30 °C |
kJ/m² |
ISO 180-1U |
60 |
55 |
| Izod notched impact strength |
23 °C |
kJ/m² |
ISO 180-1A |
10 |
20 |
| Izod notched impact strength |
-30 °C |
kJ/m² |
ISO 180-1A |
<10 |
<10 |
| Flexural modulus |
2 mm/min |
MPa |
ISO 178-A |
8500 |
5000 |
| Flexural strength |
2 mm/min |
MPa |
ISO 178-A |
270 |
160 |
| Flexural strain at flexural strength |
2 mm/min |
% |
ISO 178-A |
4.0 |
6.0 |
| Flexural stress at 3.5 % strain |
2 mm/min |
MPa |
ISO 178-A |
260 |
140 |
| C Puncture maximum force |
23 °C |
N |
ISO 6603-2 |
1000 |
1230 |
| C Puncture maximum force |
-30 °C |
N |
ISO 6603-2 |
860 |
|
| C Puncture energy |
23 °C |
J |
ISO 6603-2 |
3 |
6 |
| C Puncture energy |
-30 °C |
J |
ISO 6603-2 |
3 |
|
| Ball indentation hardness |
|
N/mm² |
ISO 2039-1 |
210 |
100 |
| Thermal properties |
|
|
|
|
|
| C Melting temperature |
10 °C/min |
°C |
ISO 11357-1,-3 |
222 |
|
| C Temperature of deflection under load |
1.80 MPa |
°C |
ISO 75-1,-2 |
200 |
|
| C Temperature of deflection under load |
0.45 MPa |
°C |
ISO 75-1,-2 |
215 |
|
| Vicat softening temperature |
50 N; 120 °C/h |
°C |
ISO 306 |
> 200 |
|
| C Coefficient of linear thermal expansion, parallel |
23 to 55 °C |
10-4/K |
ISO 11359-1,-2 |
0.2 |
|
| C Coefficient of linear thermal expansion, transverse |
23 to 55 °C |
10-4/K |
ISO 11359-1,-2 |
1.0 |
|
| C Burning behavior UL 94 |
1.5 mm |
Class |
UL 94 |
HB |
|
| C Burning behavior UL 94 |
0.75 mm |
Class |
UL 94 |
HB |
|
| C Oxygen index |
Method A |
% |
ISO 4589-2 |
22 |
|
| Glow wire test (GWFI) |
1.5 mm |
°C |
IEC 60695-2-12 |
700 |
|