Features
- LLDPE Hexene copolymer
- Outstanding mechanical properties and unitization holding force
Applications
- Cast stretch film for pallet
- High-end film
| Typical properties (not to be construed as specifications) | Value (English) | Value (SI) | Method | |
|
Resin Properties |
Melt Index (190°C/2.16kg) | 2.0 g/10min | 2.0 g/10min | ASTM D1238 |
| Density | 0.918 g/cm3 | 0.918 g/cm3 | ASTM D792 | |
| Base Density(1) | 0.918 g/cm3 | 0.918 g/cm3 | Sasol Method | |
|
Film Properties |
Tensile strength at yield MD | 1540 psi | 10.6 MPa | ASTM D882 |
| Tensile strength at yield TD | 1640 psi | 11.3 MPa | ASTM D882 | |
| Tensile strength at break MD | 8070 psi | 55.7 MPa | ASTM D882 | |
| Tensile strength at break TD | 6850 psi | 47.2 MPa | ASTM D882 | |
| Tensile Elongation at break MD | 480 % | 480 % | ASTM D882 | |
| Tensile Elongation at break TD | 890 % | 890 % | ASTM D882 | |
| 1% Secant Modulus MD | 22500 psi | 156 MPa | ASTM D882 | |
| 1% Secant Modulus TD | 24300 psi | 163 MPa | ASTM D882 | |
| Elmendorf Tear Strength MD | 280 g/mil | 280 g/25.4 µm | ASTM D1922 | |
| Elmendorf Tear Strength TD | 813 g/mil | 813 g/25.4 µm | ASTM D1922 | |
| Dart Drop Impact Strength (F50) | 165 g/mil | 165 g/25.4 µm | ASTM D1709A | |
| Haze | 2.5% | 2.5% | ASTM D1003 | |
| Gloss (45°) | 95% | 95% | ASTM D2457 | |
Specification: LL FILM-SASOL-HF1820X
|