Product Description
Enable™ 3505MC performance polymer resin is an ethylene 1-hexene copolymer. It can be employed in medium and high density jacketing. It has a good balance of mechanical strength, abrasion and strong environmental stress crack resistance (ESCR). Sufficient carbon black or UV stabilizer should be added to meet cable jacketing specifications
| Resin Properties | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Density / Specific Gravity | 0.935 | g/cm³ | 0.935 | g/cm³ | ASTM D792 |
| Melt Index (190°C/2.16 kg) | 0.50 | g/10 min | 0.50 | g/10 min | ASTM D1238 |
| Peak Melting Temperature | 254 | °F | 123 | °C | ExxonMobil Method |
| Thermal Typical Value | (English) | Typical Value | (SI) | Test Based On | |
| Vicat Softening Temperature 247 | °F | 120 | °C | ExxonMobil | |
| Method | |||||
| Molded Properties | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Tensile Strength at Yield
2.0 in/min (50 mm/min) |
2800 |
psi |
19 |
MPa |
ExxonMobil Method |
| Tensile Strength at Break
2.0 in/min (50 mm/min) |
5700 |
psi |
39 |
MPa |
ExxonMobil Method |
| Elongation at Yield (2.0 in/min (51 mm/min)) | 10 | % | 10 | % | ExxonMobil Method |
| Elongation at Break
(2.0 in/min (50 mm/min)) |
790 | % | 790 | % | ExxonMobil Method |
| Flexural Modulus – 1% Secant
Procedure A, 0.051 in/min (1.3 mm/min) |
80000 |
psi |
550 |
MPa |
ExxonMobil Method |
| Environmental Stress-Crack Resistance
Condition B, 10% Igepal, F50 |
> 1000 |
hr |
> 1000 |
hr |
ExxonMobil Method |
| Durometer Hardness (Shore D, 15 sec) | 54 | 54 | ExxonMobil Method | ||
| Electrical | Typical Value | (English) | Typical Value | (SI) | Test Based On |
| Volume Resistivity (500 V) | 7.5E+14 | ohms·m | 7.5E+14 | ohms·m | IEC 62631-3-1 |
| Relative Permittivity (1 MHz) | 2.28 | 2.28 | IEC 62631-2-1 | ||
| Dissipation Factor (1 MHz) | 1.3E-4 | 1.3E-4 | IEC 62631-2-1 | ||