| Physical Nominal Value | (English) | Nominal Value | (SI) | Test Method | |
| Density | 0.921 | g/cm³ | 0.921 | g/cm³ | ASTM D792 |
| Melt Index (190°C/2.16 kg) | 0.25 | g/10 min | 0.25 | g/10 min | ISO 1133 |
| Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Film Thickness – Tested | 4 | mil | 100 | µm | |
| Tensile Modulus
2% Secant, MD : 3.9 mil (100 µm) |
18600 |
psi |
128 |
MPa |
ISO 527-3 |
| 2% Secant, TD : 3.9 mil (100 µm) | 18600 | psi | 128 | MPa | |
| Tensile Stress
MD : Yield, 3.9 mil (100 µm) |
1330 |
psi |
9.20 |
MPa |
ISO 527-3 |
| TD : Yield, 3.9 mil (100 µm) | 1100 | psi | 7.60 | MPa | |
| MD : Break, 3.9 mil (100 µm) | 3050 | psi | 21.0 | MPa | |
| TD : Break, 3.9 mil (100 µm) | 2970 | psi | 20.5 | MPa | |
| Tensile Elongation
MD : Break, 3.9 mil (100 µm) |
470 |
% |
470 |
% |
ASTM D882 |
| TD : Break, 3.9 mil (100 µm) | 530 | % | 530 | % | |
| Dart Drop Impact (3.9 mil (100 µm)) | 430 | g | 430 | g | ISO 7765-1/A |
| Elmendorf Tear Strength
MD : 3.9 mil (100 µm) |
270 |
g |
270 |
g |
ASTM D1922 |
| TD : 3.9 mil (100 µm) | 480 | g | 480 | g | |
| Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Vicat Softening Temperature | 205 | °F | 96.0 | °C | ASTM D1525 |
Specification: LD HEAVY-DOW-150E
|