Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Density | 0.923 | g/cm³ | 0.923 | g/cm³ | ASTM D792 |
Melt Index (190°C/2.16 kg) | 2.0 | g/10 min | 2.0 | g/10 min | ASTM D1238 |
Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Film Thickness – Tested | 2 | mil | 50 | µm | |
Tensile Strength
MD : Yield, 2.0 mil (50 µm) |
1490 |
psi |
10.3 |
MPa |
ASTM D882 |
TD : Yield, 2.0 mil (50 µm) | 1770 | psi | 12.2 | MPa | |
MD : Break, 2.0 mil (50 µm) | 3030 | psi | 20.9 | MPa | |
TD : Break, 2.0 mil (50 µm) | 2630 | psi | 18.1 | MPa | |
Tensile Elongation
MD : Break, 2.0 mil (50 µm) |
400 |
% |
400 |
% |
ASTM D882 |
TD : Break, 2.0 mil (50 µm) | 550 | % | 550 | % | |
Dart Drop Impact (2.0 mil (50 µm)) | 110 | g | 110 | g | ASTM D1709A |
Elmendorf Tear Strength
MD : 2.0 mil (50 µm) |
430 |
g |
430 |
g |
ASTM D1922 |
TD : 2.0 mil (50 µm) | 370 | g | 370 | g | |
Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Vicat Softening Temperature | 210 | °F | 99.0 | °C | ASTM D1525 |
Optical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Gloss (20°, 1.97 mil (50.0 µm)) | 66 | 66 | ASTM D2457 | ||
Haze (1.97 mil (50.0 µm)) | 7.50 | % | 7.50 | % | ASTM D1003 |
Extrusion | Nominal Value | (English) | Nominal Value | (SI) | |
Melt Temperature | 379 | °F | 193 | °C |
Specification: LD FILM-DOW-450E
|