PC+ABS-LG-HR5007A
Physical
| Properties
Specific Gravity |
Test Condition | Test Method
ASTM D792 |
Unit
– |
Typical Value
1.14 |
| Molding Shrinkage (Flow), 3.2mm | ASTM D955 | % | 0.5~0.8 | |
| Melt Flow Rate | 250℃/2.16kg | ASTM D1238 | g/10min | 5.3 |
Mechanical
| Tensile Strength, 3.2mm
@ Yield |
50mm/min |
ASTM D638 |
kg/cm2 |
580 |
| Tensile Elongation, 3.2mm
@ Yield |
50mm/min |
ASTM D638 |
% |
|
| @ Break | 50mm/min | % | >100 | |
| Flexural Strength, 3.2mm | 10mm/min | ASTM D790 | kg/cm2 | 790 |
| Flexural Modulus, 3.2mm | 10mm/min | ASTM D790 | kg/cm2 | 21,500 |
| IZOD Impact Strength, 3.2mm
(Notched) |
23℃ |
ASTM D256 |
kg·cm/cm |
65 |
| -30℃ | kg·cm/cm | 50 | ||
| Rockwell Hardness | R-Scale | ASTM D785 | – | 114 |
Thermal
| Heat Deflection Temperature, 6.4mm (Unannealed) |
18.6kg 4.6kg |
ASTM D648 |
℃ ℃ |
113 – |
| Vicat Softening Temperature | ASTM D1525 | |||
| 5kg, 50℃/h | ℃ | |||
| Ball Pressure Temperature | IEC 60695-10-2 | ℃ | ||
| Burning Rate, 3.2mm | FMVSS 302 | mm | ||
| Flammability
0.8mm |
UL94 |
class |
||
| 1.6mm
2.5mm 3.0mm |
class
class class |
HB
HB |
||
| Relative Temperature Index
Electrical |
UL 746B |
℃ |
60 |
|
| Mechanical with Impact | ℃ | 60 | ||
| Mechanical without Impact | ℃ | 60 |
Specification: PC+ABS-LG-HR5007A
|