| Physical |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Density |
0.904 |
g/cm³ |
0.904 |
g/cm³ |
ASTM D792 |
| Base Density 1 |
0.904 |
g/cm³ |
0.904 |
g/cm³ |
Dow Method |
| Melt Index (190°C/2.16 kg) |
4.0 |
g/10 min |
4.0 |
g/10 min |
ASTM D1238 |
| Films |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Film Puncture Resistance |
|
|
|
|
Dow Method |
| 0.80 mil (20 µm) |
228 |
ft·lb/in³ |
18.9 |
J/cm³ |
|
| 2.0 mil (51 µm) |
211 |
ft·lb/in³ |
17.5 |
J/cm³ |
|
| Secant Modulus |
|
|
|
|
ASTM D882 |
| 2% Secant, MD : 0.80 mil (20 µm) |
8530 |
psi |
58.8 |
MPa |
|
| 2% Secant, MD : 2.0 mil (51 µm) |
9070 |
psi |
62.6 |
MPa |
|
| 2% Secant, TD : 0.80 mil (20 µm) |
9380 |
psi |
64.7 |
MPa |
|
| 2% Secant, TD : 2.0 mil (51 µm) |
9140 |
psi |
63.0 |
MPa |
|
| Tensile Strength |
|
|
|
|
ASTM D882 |
| MD : Yield, 0.80 mil (20 µm) |
1020 |
psi |
7.00 |
MPa |
|
| MD : Yield, 2.0 mil (51 µm) |
980 |
psi |
6.76 |
MPa |
|
| TD : Yield, 0.80 mil (20 µm) |
713 |
psi |
4.92 |
MPa |
|
| TD : Yield, 2.0 mil (51 µm) |
919 |
psi |
6.34 |
MPa |
|
| MD : Break, 0.80 mil (20 µm) |
5350 |
psi |
36.9 |
MPa |
|
| MD : Break, 2.0 mil (51 µm) |
4730 |
psi |
32.6 |
MPa |
|
| TD : Break, 0.80 mil (20 µm) |
4220 |
psi |
29.1 |
MPa |
|
| TD : Break, 2.0 mil (51 µm) |
4700 |
psi |
32.4 |
MPa |
|
| Tensile Elongation |
|
|
|
|
ASTM D882 |
| MD : Break, 0.80 mil (20 µm) |
500 |
% |
500 |
% |
|
| MD : Break, 2.0 mil (51 µm) |
660 |
% |
660 |
% |
|
| TD : Break, 0.80 mil (20 µm) |
710 |
% |
710 |
% |
|
| TD : Break, 2.0 mil (51 µm) |
710 |
% |
710 |
% |
|
| Dart Drop Impact |
|
|
|
|
ASTM D1709B |
| 0.80 mil (20 µm) |
> 850 |
g |
> 850 |
g |
|
| 2.0 mil (51 µm) |
> 850 |
g |
> 850 |
g |
|
| Elmendorf Tear Strength |
|
|
|
|
ASTM D1922 |
| MD : 0.80 mil (20 µm) |
330 |
g |
330 |
g |
|
| MD : 2.0 mil (51 µm) |
960 |
g |
960 |
g |
|
| TD : 0.80 mil (20 µm) |
500 |
g |
500 |
g |
|
| TD : 2.0 mil (51 µm) |
1100 |
g |
1100 |
g |
|
| Oxygen Permeability |
|
|
|
|
ASTM D3985 |
There are no reviews yet.