DESCRIPTION
TASNEE LD 4025AS is a Low Density Polyethylene with a Melt Flow Rate of 4.0 g/10min (190°C/2.16kg).
TASNEE LD 4025AS is mainly recommended for thin-gauge with high clarity film applications. It contains both slip agent and anti-blocking additives and has a suitable molecular structure to produce film with excellent mechanical properties.
TASNEE LD 4025AS can be easily processed on all types of extruders designed for polyethylene. The melt temperature is suggested to be in the range of 150 – 190°C. Excellent properties of the film are achieved with a blow – up ratio of 2.5:1 and recommended film thickness range from 15 to 40 μm.
TYPICAL APPLICATIONS:
Shrink Film, Food Packaging Film, Blow Film and Cast Film.
PRODUCT CHARATERISTICS
Features: Anti-Blocking and Slip Additives, Good Optical Properties, Good Processability, Low Friction and Good Stiffness.
TYPICAL PROPERTIES
| Physical | Method | Unit | Values |
| Density | ISO 1183 | g/cm3 | 0.925 |
| Melt Flow Rate (190°C/2.16 kg) | ISO 1133 | g/10min | 4.0 |
| Melting Temperature | ISO 3146 | °C | 111 |
| Vicat Softening Temperature (A50 (50 OC/h 10N)) | ISO 306 | °C | 92 |
| Mechanical | Method | Unit | Values(1) |
| Tensile Modulus | ISO 527-1,-2 | MPa | 260 |
| Tensile Stress @ Yield | ISO 527-1,-2 | MPa | 11 |
| Tensile Strain @ Break (MD / TD) | ISO 527-1,-3 | % | 300 / 600 |
| Tensile Strength (MD / TD) | ISO 527-1,-3 | MPa | 22 / 15 |
| Dart Drop Impact (50 µm) | ASTM D 1709 | g | 100 |
| Coefficient of Friction | ISO 8295 | % | < 20 |
| Optical | Method | Unit | Values(1) |
| Haze | ASTM D 1003 | % | < 9 |
| Gloss (20o)
(60o) |
ASTM D 2457 | GU GU | > 60
> 105 |
Specification: LD BLOW-TASNEE-4025AS
|