HD-MARLEX-HMN6060

Nominal Physical Properties (1)	English	SI	Method
Density	—-	0.962 g/cm3	ASTM D1505
Flow Rate (MI, 190 °C/2.16 kg)	—-	6.5 g/10 min	ASTM D1238
Flexural Modulus, 1 % Secant, 16:1 span:depth, 0.5 in/min	230,000 psi	1,586 MPa	ASTM D790
Flexural Modulus, Tangent, 16:1 span:depth, 0.5 in/min	250,000 psi	1,724 MPa	ASTM D790
Tensile Strength at Yield, 2 in/min, Type IV bar	4,700 psi	32 MPa	ASTM D638
Tensile Elongation at Yield, 2 in/min, Type IV bar	8 %	8 %	ASTM D638
Tensile Elongation at Break, 2 in/min, Type IV bar	> 900 %	> 900 %	ASTM D638
ESCR, Condition B (100 % Igepal), F50	15 h	15 h	ASTM D1693
Notched Izod Impact, 73.4 °F Test Temperature	0.6 ft·lbf/in	35 J/m	ASTM D256
High Speed Impact Peak Energy, 21.6 ft/sec, 73.4 °F	14 ft·lbf	19 J/m	ASTM D3763
High Speed Impact Total Energy, 21.6 ft/sec, 73.4 °F	25 ft·lbf	34 J/m	ASTM D3763
Durometer Hardness, Type D (Shore D)	66	66	ASTM D2240
Vicat Softening Temperature, Loading 1, Rate A	261 °F	127 °C	ASTM D1525
Heat Deflection Temperature, 66 psi, Method A	190 °F	88 °C	ASTM D648
Heat Deflection Temperature, 264 psi, Method A	124 °F	51 °C	ASTM D648
Brittleness Temperature, Type A, Type I specimen	< -103 °F	< -75 °C	ASTM D746

Specification: HD-MARLEX-HMN6060

ALPHA	M
Group	HD
Class	HD
GRADE	HMN6060
MFI	6.5
NOTES	HD MOULDING
PROCESS	MOULDING
Country	India, Malaysia
Tds-Name	MarlexHMN6060Polyethylene_0_0.pdf
Tds-Url	https://sourcechatapp-media.s3.ap-south-1.amazonaws.com/5d974e7bdc0abf2e84b0e23a/MarlexHMN6060Polyethylene_0_0.pdf
D-Type	S
Brand	M>MARLEX