Features
- High molecular weight hexene copolymer HDPE with a bimodal molecular weight
- Excellent draw-down for thin films.
- Bubble stability for high
- Good balance of stiffness and toughness
Potential Applications
- Thin films for trash can liners, t-shirt bags, merchandise bags, produce bags and roll
- Thick film for multi use
Typical properties (not to be construed as specifications) | Value (English) | Value (SI) | Method | |
Resin Properties |
Melt Index (190°C/2.16kg) | 0.057 g/10min | 0.057 g/10min | ASTM D1238 |
High Load Melt Index (190°C/21.6 kg load) | 9.0 g/10min | 9.0 g/10min | ASTM D1238 | |
Density | 0.952 g/cm³ | 0.952 g/cm³ | ASTM D4883 | |
Physical Properties |
Tensile Strength at Yield MD | 4500 psi | 31 MPa | ASTM D882 |
Tensile Strength at Yield TD | 3900 psi | 27 MPa | ASTM D882 | |
Tensile Strength at Break MD | 11000 psi | 76 MPa | ASTM D882 | |
Tensile Strength at Break TD | 7000 psi | 48 MPa | ASTM D882 | |
Elongation at Break MD | >250 % | >250 % | ASTM D882 | |
Elongation at Break TD | >350 % | >350 % | ASTM D882 | |
1% Secant Modulus MD | 112000 psi | 772 MPa | ASTM D882 | |
1% Secant Modulus TD | 139000 psi | 958 MPa | ASTM D882 | |
Dart Drop Impact | 350 g | 350 g | ASTM D1709 | |
Elmendorf Tear MD | 37 g | 37 g | ASTM 1922 | |
Elmendorf Tear TD | 83 g | 83 g | ASTM 1922 |
Specification: HD HM-SASOL-HD5208FLX
|