Nominal Resin Properties(1,2) |
Value (SI Units) |
Method |
Density |
0.948 g/cm3 |
ASTM D1505 |
Flow Rate (HLMI, 190/21.6) |
9 g/10 min |
ASTM D1238 |
Tensile Strength at Yield, 2 in/min, Type IV bar |
25 MPa |
ASTM D638 |
Elongation at Break, 2 in/min, Type IV bar |
700 % |
ASTM D638 |
Flexural Modulus, Tangent, 16:1 span:depth, 0.5 in/min |
1,200 MPa |
ASTM D790 |
ESCR, Condition B (100% Igepal), F50 |
>600 h |
ASTM D1693 |
Durometer Hardness, Type D (Shore D) |
68 |
ASTM D2240 |
Vicat Softening Temperature, Loading 1, Rate A |
126 °C |
ASTM D1525 |
Heat Deflection Temperature, 66 psi, Method A |
78 °C |
ASTM D648 |
Brittleness Temperature, Type A, Type I specimen |
<-75 °C |
ASTM D746 |
Tensile Impact, Type S bar |
190 kJ/m2 |
ASTM D1822 |