E5201S is a broad molecular weight distribution HDPE, produced by the Mitsui CX Process. The Grade is used for General Purpose Blow Molding Applications.
E5201S combines exceptional processability and excellent mechanical properties.
| Property |
Test Method |
Unit |
Value |
| Melt Flow Index (2.16 kg, 190°C) |
ASTM D 1238 |
g/10 min |
0.35 |
| Density (23°C) |
ASTM D 1505 |
g/cm3 |
0.958 |
| Physical Property |
|
|
|
| Tensile Strength at Yield |
|
MPa |
25 |
| Elongation at Yield |
ASTM D 638 |
% |
11 |
| Tensile Strength at Break |
(50 mm/min) |
MPa |
36 |
| Elongation at Break |
|
% |
>600 |
| Notched Izod Impact Strength (23°C) |
ASTM D 256A |
J/m |
150 |
| Flexural Modulus |
ASTM D 790A |
MPa |
1100 |
| Hardness |
ASTM D 2240 |
Shore D |
61 |
| ESCR (F50, 10% Igepal soln. v/v) |
ASTM D 1693B |
Hr |
200 |
| Vicat Softening Point(10N) |
ASTM D 1525 |
°C |
129 |
| Heat Deflection Temperature (0.455 MPa) |
ASTM D 648 |
°C |
80 |
| DSC Melting Temperature |
ASTM D 3418 |
°C |
130 |
| Suggested Processing Conditions |
| Barrel Temperature |
°C |
150/160/160 |
| Die Temperature |
°C |
160 – 165 |
| Parison Temperature |
°C |
165 – 170 |